TAISOX 2114
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Formosa Plastics Corporation |
| Trademark: | TAISOX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | G9rlci_TAISOX-2114.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TAISOX 2114 is a linear low density polyethylene material,. This product is available in North America, Europe or Asia Pacific region. The processing method is blow molded film. The main features of TAISOX 2114 are:
The typical application fields of TAISOX 2114 are: movies |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.918 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 38 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 38 µm, blown film | 157 | MPa | ASTM D882 |
| 1% secant, TD : 38 µm, blown film | 196 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 38 µm, blown film | 9.81 | MPa | ASTM D882 |
| TD : Yield, 38 µm, blown film | 10.8 | MPa | ASTM D882 |
| MD : Broken, 38 µm, blown film | 49.0 | MPa | ASTM D882 |
| TD : Broken, 38 µm, blown film | 44.1 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 38 µm, blown film | 620 | % | ASTM D882 |
| TD : Broken, 38 µm, blown film | 810 | % | ASTM D882 |
| Dart Drop Impact (38 µm, Blown Film) | 610 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 38 µm, blown film | 460 | g | ASTM D1922 |
| TD : 38 µm, blown film | 760 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 93.0 | °C | ASTM D1525 |
| Melting Temperature | 121 | °C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 38.0 µm, Blown Film) | 51 | ASTM D2457 | |
| Clarity | 60.0 | ASTM D1746 | |
| Haze (38.0 µm, Blown Film) | 15 | % | ASTM D1003 |
| Additional Information |
|---|
| Blow Up Ratio: 2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom PP6430 B9 | Spartech Polycom | PP, Unspecified | Spartech |
| Viton® GFLT-600S | DuPont Performance Elastomers | Fluorelastomer | Viton® |
| AKROMID® A3 1 L natural (4800) | AKRO-PLASTIC GmbH | Nylon 66+PP | AKROMID® |
| Plaslube® PA6/6 GF30 TL15 BK | Techmer Engineered Solutions | Nylon 66 | Plaslube® |
| Clyrell RC213M | LyondellBasell Industries | PP Random Copolymer | Clyrell |