LNP™ THERMOCOMP™ LF004E compound
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | G9SSuZ_LNPTHERMOCOMPLF004Ecompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LNP THERMOCOMP LF004E is a compound based on Polyetheretherketone resin containing Glass Fiber. Added features include: Easy Molding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.42 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 120 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 1.8 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 7000 | MPa | ISO 178 |
| Flexural Stress | 196 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 2(23°C) | 6.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 25 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4(1.8 MPa, Unannealed, 64.0 mm Span) | > 280 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 - 149 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 349 - 360 | °C | |
| Middle Temperature | 366 - 377 | °C | |
| Front Temperature | 382 - 393 | °C | |
| Processing (Melt) Temp | 382 - 388 | °C | |
| Mold Temperature | 138 - 166 | °C | |
| Back Pressure | 0.344 - 0.689 | MPa | |
| Screw Speed | 60 - 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultradur® B 4300 G6 LS BK15073 | BASF Corporation | PBT | Ultradur® |
| Unilex™ UP 8002 | United Polychem | PP Homopolymer | Unilex™ |
| ZEONEX® K26R | Zeon Corporation | COP | ZEONEX® |
| Sylvin 9302-70 WHITE 1264 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 9077-95LMW Yellow 4186 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |