NORYL GTX™ GTX673 resin
| Category: | PPE+PS+Nylon , Polyphenylene Ether + PS + Nylon |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | NORYL GTX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | G8nCHb_NORYL-GTX-GTX673-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Conductive NORYL GTX resin designed for profile extrusion. This grade can be electrostatic or powder coat painted without the need for a primer. In addition, its high heat capability allows it to be painted on the same line as metal. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/5.0 kg) | 7.8 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (300°C/5.0 kg) | 7.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 1.3 - 1.5 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 4.0 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.40 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2420 | MPa | ASTM D638 |
| -- | 2670 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 65.0 | MPa | ASTM D638 |
| Yield | 66.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 63.0 | MPa | ASTM D638 |
| Fracture | 64.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 3.8 | % | ASTM D638 |
| Yield | 4.0 | % | ISO 527-2/50 |
| Fracture 5 | 6.1 | % | ASTM D638 |
| Fracture | 7.1 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 6 | 2520 | MPa | ASTM D790 |
| -- 7 | 2470 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 103 | MPa | ISO 178 |
| Yield, 50.0mm span 8 | 100 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 12 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 58 | J/m | ASTM D256 |
| 23°C | 110 | J/m | ASTM D256 |
| -30°C 10 | 6.0 | kJ/m² | ISO 180/1A |
| 23°C 11 | 11 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 5.00 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 187 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 12 | 184 | °C | ISO 75-2/Bf |
| Vicat Softening Temperature | |||
| -- | 197 | °C | ASTM D1525, ISO 306/B50 10 13 |
| -- | 198 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 7.6E-5 | cm/cm/°C | ASTM E831 |
| Flow : 23 to 60°C | 8.1E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 7.8E-5 | cm/cm/°C | ASTM E831 |
| Lateral : 23 to 60°C | 8.6E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+3 - 1.0E+4 | ohms·cm | Internal method |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 105 - 110 | °C | |
| Drying Time | 8.0 | hr | |
| Suggested Max Moisture | 0.030 | % | |
| Cylinder Zone 1 Temp. | 245 - 260 | °C | |
| Cylinder Zone 2 Temp. | 245 - 260 | °C | |
| Cylinder Zone 3 Temp. | 245 - 260 | °C | |
| Cylinder Zone 4 Temp. | 245 - 260 | °C | |
| Adapter Temperature | 245 - 260 | °C | |
| Melt Temperature | 245 - 260 | °C | |
| Die Temperature | 245 - 260 | °C | |
| Calibration Temp, First | 35.0 - 75.0 | °C |
| Extrusion instructions |
|---|
| Drying Time (Cumulative): 24 hrsWater Bath Temperature: 35 - 50 °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | Type 1, 50mm/min |
| 5 . | Type 1, 50mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Propilven S-701 | Propilven, S.A. | PP Homopolymer | Propilven |
| Xuchuan XCS-80P | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Boltaron 4004 BoltaMask | Boltaron Performance Products | PVC, Unspecified | Boltaron |
| Axiall PVC 3605 | Axiall Corporation | PVC, Rigid | Axiall PVC |
| Fainplast PVC PMP 78/5 | Fainplast Compounds S.r.l | PVC+PUR | Fainplast PVC |