Beta (ß)-PP™ BE60-7032-02
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Borealis AG |
| Trademark: | Beta (ß)-PP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | G8iB1w_Beta--PP-BE60-7032-02.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
BE60-7032-02 is a high molecular weight, low melt flow rate polypropylene homopolymer with fine grained ß-modification crystalline structure leading to excellent impact strength even at low temperatures, increased hydrostatic strength and improved chemical resistance. The material is coloured grey based on RAL 7032. BE60-7032-02 is recommended for pressure pipes and fittings, chemical engineering components, extruded and compression moulded sheets, filter plates and solid rods. BE60-7032-02 has improved sagging properties compared to Beta (ß)-PP™ BE60-7032. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.905 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/5.0 kg | 0.50 | g/10 min | ISO 1133 |
| 230°C/2.16 kg | 0.30 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1300 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 30.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 10 | % | ISO 527-2/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 5.0 | kJ/m² | ISO 179/1eA |
| 23°C | 50 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 96.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 92.0 | °C | ISO 306/B50 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 190 - 230 | °C | |
| Cylinder Zone 2 Temp. | 190 - 230 | °C | |
| Cylinder Zone 3 Temp. | 190 - 230 | °C | |
| Cylinder Zone 4 Temp. | 190 - 230 | °C | |
| Cylinder Zone 5 Temp. | 190 - 230 | °C | |
| Melt Temperature | 200 - 230 | °C | |
| Die Temperature | 200 - 230 | °C |
| Extrusion instructions |
|---|
| Head Temperature: 200 to 230°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Reny® 1022HS | Mitsubishi Engineering-Plastics Corp | PARA | Reny® |
| Nylfor® A2 E2/3E NATURALE | SO.F.TER. SPA | Nylon 66 | Nylfor® |
| INSULCAST® RTVS 16 | ITW Polymers Coatings North America | Silicone Rubber, RTV-2 | INSULCAST® RTVS |
| PIVINEL™ VFR-5013 | HELLENIC CABLES S.A. | PVC, Unspecified | PIVINEL™ |
| Kepex® 4345GF | Korea Engineering Plastics Co., Ltd | PBT | Kepex® |