Order Products : sales@su-jiao.com
Kingfa API-1025
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Kingfa |
| Trademark: | Kingfa |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | G89gcg_Kingfa-API-1025.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PP-EPDM-T10 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.960 - 1.00 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 23 - 28 | g/10 min | ISO 1133 |
| Molding Shrinkage (23°C) | 0.012 - 0.013 | % | Internal method |
| Ash Content 1(750°C) | 10 - 13 | % | ISO 3451 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Weather Resistance 2 | 4.00 - 5.00 | SAE J1960 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 24.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 25 | % | ISO 527-2/50 |
| Flexural Modulus 3 | 1700 | MPa | ISO 178 |
| Flexural Stress 4 | 34.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 5(23°C) | 6.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, unannealed, 4.00mm span) | 115 | °C | ISO 75-2/B |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating 6 | HB | ISO 3795 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 0.0 - 2.0 | hr | |
| Rear Temperature | 190 - 210 | °C | |
| Middle Temperature | 205 - 230 | °C | |
| Front Temperature | 215 - 240 | °C | |
| Processing (Melt) Temp | 220 - 245 | °C | |
| Mold Temperature | 30.0 - 60.0 | °C | |
| Injection Rate | Slow-Moderate | ||
| Back Pressure | 0.350 | MPa |
| Injection instructions |
|---|
| Processing Temp. Limit: 250°C |
| Note Message | |
|---|---|
| 1 . | 30 min |
| 2 . | 250 kJ/m² |
| 3 . | 2.0 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | 4 mm |
| 6 . | 360×100×3 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 600 GB 20 | RTP Company | ABS | RTP |
| Yanshan PE LD100BW | SINOPEC Beijing Yanshan Petrochemical | LDPE | Yanshan PE |
| BCC Resins BC 9060 | BCC Products Inc. | Silicone | BCC Resins |
| Haysite SMC 42000 | Haysite Reinforced Plastics | Polyester, TS | Haysite SMC |
| IROCOAT® CA-151HT | Huntsman Corporation | TPU, Unspecified | IROCOAT® |