TAROMID A 280 G3 K3
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TAROMID A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | G7PQgv_TAROMID-A-280-G3-K3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 66 medium viscosity 30% glass beads/glass fibres reinforced, very good surface finish and dimensional stability. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.33 - 1.35 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (280°C/2.16 kg) | 15 | g/10 min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Vertical flow direction | 0.80 - 1.0 | % | Internal method |
| Flow direction | 0.45 - 0.55 | % | Internal method |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 0.50 | % | ISO 62 |
| Saturated, 23°C | 5.3 | % | ISO 62 |
| Granule Humidity 1 | % |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Reinforcement Content 2(750°C) | 30 | % | ISO 3451 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5700 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 100 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 5.0 | % | ISO 527-2/50 |
| Flexural Modulus 3 | 5400 | MPa | ISO 178 |
| Flexural Stress 4 | 160 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 18 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 45 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5(1.8 MPa, Unannealed) | 217 | °C | ISO 75-2/A |
| Continuous Use Temperature | IEC 60216 | ||
| -- 6 | 90.0 | °C | IEC 60216 |
| -- 7 | 130 | °C | IEC 60216 |
| Vicat Softening Temperature | |||
| -- | 245 | °C | ISO 306/A50 |
| -- | 230 | °C | ISO 306/B50 |
| Ball Pressure Test (205°C) | Pass | IEC 60695-10-2 | |
| Melting Temperature | 255 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 7.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength (2.00 mm) | 21 | kV/mm | IEC 60243-1 |
| Dielectric Constant | 3.80 | IEC 60250 | |
| Comparative Tracking Index | IEC 60112 | ||
| Solution a | 500 | V | IEC 60112 |
| Solution B | 300 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 750 | °C | IEC 60695-2-12 |
| Oxygen Index | 27 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 90.0 | °C | |
| Drying Time | 1.0 | hr | |
| Processing (Melt) Temp | 250 - 280 | °C | |
| Mold Temperature | 70.0 - 90.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Pre-heat Temperature: 80 to 100°CPre-heat Time: 3 hr |
| Note Message | |
|---|---|
| 1 . | TARO 002 |
| 2 . | 1 hr |
| 3 . | 1.0 mm/min |
| 4 . | 1.0 mm/min |
| 5 . | 120°C/hr |
| 6 . | 20,000 hr, 120 H |
| 7 . | Short term, 160 H |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1499 P X 102560 A | RTP Company | PPSU | RTP |
| PRL PPX/NY-G30 | Polymer Resources Ltd. | PPE+PS+Nylon | PRL |
| Sinvicomp SBF3748 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| HiFill® PA6 0365 01 BK | Techmer Engineered Solutions | Nylon 6 | HiFill® |
| LUVOCOM® 80-7653 VP | Lehmann & Voss & Co. | Acetal (POM) Copolymer | LUVOCOM® |