Westlake LDPE EF606
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Westlake Chemical Corporation |
| Trademark: | Westlake LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | G6ogzF_Westlake-LDPE-EF606.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Westlake EF606 is a LDPE resin suggested for use in multiwall and general purpose liners, and for use as a blend resin in general purpose packaging applications. It has excellent processability, and is an excellent bubble stabilizer in LLDPE rich blends. Application/Uses: Trash bags General purpose lin Multiwall liners Industrial liners |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.919 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.2 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 51 | µm | |
| secant modulus 1 | ASTM D882 | ||
| 1% secant, MD : 51 µm, blown film | 152 | MPa | ASTM D882 |
| 1% secant, TD : 51 µm, blown film | 193 | MPa | ASTM D882 |
| Tensile Strength 2 | ASTM D882 | ||
| MD : Broken, 51 µm, blown film | 26.9 | MPa | ASTM D882 |
| TD : Broken, 51 µm, blown film | 17.9 | MPa | ASTM D882 |
| Tensile Elongation 3 | ASTM D882 | ||
| MD : Broken, 51 µm, blown film | 300 | % | ASTM D882 |
| TD : Broken, 51 µm, blown film | 600 | % | ASTM D882 |
| Dart Drop Impact 4(51 µm, Blown Film) | 130 | g | ASTM D1709 |
| Additional Information |
|---|
| Test specimens for blown film: nominal thickness 2.0 mils; blow up ratio 2.5:1, die gap 35 mils.Melt temperatures of 360° F - 400° F are recommended for Westlake Chemical EF606 with blow-up ratios of 1.5:1 or higher. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 182 - 204 | °C |
| Note Message | |
|---|---|
| 1 . | Test run at 23°C (73°F) and 50% relative humidity |
| 2 . | Test run at 23°C (73°F) and 50% relative humidity |
| 3 . | Test run at 23°C (73°F) and 50% relative humidity |
| 4 . | Test run at 23°C (73°F) and 50% relative humidity |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® HDPE M1053 | Saudi Basic Industries Corporation (SABIC) | HDPE | SABIC® HDPE |
| NEOFLON™ NC-1539N | DAIKIN AMERICA, INC. | FEP | NEOFLON™ |
| Ferro PP TPP13AC03BK | Ferro Corporation | PP Homopolymer | Ferro PP |
| Hylon® N2000MDHL | Ravago Manufacturing Americas, LLC | Nylon 6 | Hylon® |
| Karina ORANGE COLOR CONCENTRATE 32/19-G | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |