VYPET VNT 835
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | Lavergne Group |
| Trademark: | VYPET |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | G6XgXM_VYPET-VNT-835.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
VYPET VNT 835 is a 35% mineral and fiberglass reinforced PET injection molded compound designed for structural applications. Features
Typical Applications
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.56 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 2.00mm | 0.40 | % | ASTM D955 |
| Transverse flow : 2.00mm | 0.80 | % | ASTM D955 |
| Vertical flow direction : 2.00mm | 0.80 | % | ISO 294-4 |
| Flow direction : 2.00mm | 0.40 | % | ISO 294-4 |
| Ash Content | |||
| -- | 35 | % | ISO 3451-1 |
| -- | 35 | % | ASTM D2854 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield 1 | 120 | MPa | ASTM D638 |
| Yield | 120 | MPa | ISO 527-2/5 |
| Flexural Modulus | |||
| -- 2 | 9900 | MPa | ASTM D790 |
| -- 3 | 9700 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 4 | 185 | MPa | ASTM D790 |
| -- 5 | 175 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 75 | J/m | ASTM D256 |
| 23°C | 7.0 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 213 | °C | ASTM D648, ISO 75-2/A |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 260 - 270 | °C | |
| Middle Temperature | 265 - 275 | °C | |
| Front Temperature | 270 - 295 | °C | |
| Nozzle Temperature | 275 - 300 | °C | |
| Processing (Melt) Temp | 275 - 300 | °C | |
| Mold Temperature | 95.0 - 120 | °C | |
| Injection Pressure | 55.0 - 85.0 | MPa | |
| Injection Rate | Fast | ||
| Screw Speed | 50 - 75 | rpm |
| Injection instructions |
|---|
| Back Pressure: Low |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 1.3 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVAMID® 6 GF 33 | Plastcom | Nylon 6 | SLOVAMID® 6 |
| FLEXITEQ™ F75A110 | Marplex Australia Pty. Ltd. | TPV | FLEXITEQ™ |
| Elastron® G G501.A23.N | Elastron USA, Inc. | SEBS | Elastron® G |
| EMERGE™ PC/ABS 7590 | Trinseo | PC+ABS | EMERGE™ |
| Osterlene® HIPS03.503 | Osterman & Company | PS (HIPS) | Osterlene® |