Hostalen PP H1022 12
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hostalen PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | G6W7ck_Hostalen-PP-H1022-12.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Hostalen PP H1022 12 is a black coloured, basic stabilisation polypropylene blockcopolymer with high melt viscosity and excellent low-temperature impact strength. The material Hostalen PP H1022 12 has not been tested and therefore has not been certified for pressure applications. For further details about the suitable applications for this material please contact LyondellBasell. Hostalen PP H1022 12 is not intended for medical and pharmaceutical applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.908 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/5.0 kg | 0.50 | g/10 min | ISO 1133 |
| 230°C/2.16 kg | 0.30 | g/10 min | ISO 1133 |
| 230°C/5.0 kg | 1.3 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 3 sec) | 66 | ISO 868 | |
| Ball Indentation Hardness (H 132/30) | 50.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - Secant (23°C) | 1400 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 30.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield, 23°C) | 13 | % | ISO 527-2/50 |
| Tensile Creep Modulus | ISO 899-1 | ||
| 1 hr | 1020 | MPa | ISO 899-1 |
| 1000 hr | 500 | MPa | ISO 899-1 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 4.0 | kJ/m² | ISO 179 |
| 0°C | 21 | kJ/m² | ISO 179 |
| 23°C | 120 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 75.0 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 52.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 157 | °C | ISO 306/A50 |
| -- | 75.0 | °C | ISO 306/B50 |
| Melting Temperature (DSC) | 165 | °C | ISO 3146 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 200 - 280 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 200 - 230 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx 80S7301 | The Matrixx Group, Inc. | PET | Matrixx |
| APEX® 94-A0098C-45 | Teknor Apex Company | PVC, Flexible | APEX® |
| ASI POLYPROPYLENE 1500X-01 | A. Schulman Inc. | PP Impact Copolymer | ASI POLYPROPYLENE |
| Lusin® Clean 1010 | Chem-Trend L.P. | TP, Unspecified | Lusin® |
| NORYL™ SA9000 resin | SABIC Innovative Plastics | PPE | NORYL™ |