LNP™ THERMOCOMP™ 9X98071 compound
| Category: | Nylon 610 , Polyamide 610 |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | G6UguV_LNP-THERMOCOMP-9X98071-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP 9X98071 is a compound based on PA 6/10 resin containing Carbon Fiber. Added features include; Electrically Conductive. Also known as: LNP* THERMOCOMP* Compound PDX-98071 Product reorder name: 9X98071 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.16 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 170 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 3.7 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 9400 | MPa | ISO 178 |
| Flexural Stress | 225 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 2(23°C) | 12 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 60 | kJ/m² | ISO 180/1U |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+3 to 1.0E+5 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 249 to 260 | °C | |
| Middle Temperature | 266 to 277 | °C | |
| Front Temperature | 277 to 288 | °C | |
| Processing (Melt) Temp | 266 to 277 | °C | |
| Mold Temperature | 82.2 to 93.3 | °C | |
| Back Pressure | 0.344 to 0.689 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| FERREX® GPP20CG42HB BLUE | Ferro Corporation | PP Homopolymer | FERREX® |
| IROGRAN® A 85 P 5350 | Huntsman Corporation | TPU-Polyester | IROGRAN® |
| Osterlene® PPH-38-.5 | Osterman & Company | PP Homopolymer | Osterlene® |
| Vydyne® R525J BK0722 | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| TECHNYL® C 216 V50 BLACK Z | Solvay Engineering Plastics | Nylon 6 | TECHNYL® |