Prime Polypro™ F113G
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Prime Polymer Co., Ltd. |
| Trademark: | Prime Polypro™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | G5afex_Prime-Polypro-F113G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Prime Polypro™ F113G is a Polypropylene Homopolymer (PP Homopolymer) product. It can be processed by film extrusion or injection molding and is available in Asia Pacific, Europe, or North America. Applications of Prime Polypro™ F113G include fabrics/fibers, film, household applications and yarn. Primary characteristic: rigid. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.910 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.0 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | 100 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1600 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 37.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 120 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 5.5 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 110 | °C | ISO 75-2/B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen RP344N | PolyMirae | PP Random Copolymer | Moplen |
| ADENE OCJB | A.D. Compound spa | PP Homopolymer | ADENE |
| Braskem PE LL-118 | Braskem | LLDPE | Braskem PE |
| Cevian®-V CGR30F | Daicel Polymer Ltd. | ABS | Cevian®-V |
| 3M™ Dyneon™ Fluoroelastomer FE 5622Q | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroelastomer |