Cellophane™ 500PUT
| Category: | Cellulose, Regenerated , Regenerated Cellulose |
| Manufacturer: | Innovia Films Ltd. |
| Trademark: | Cellophane™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | G5aW9N_Cellophane-500PUT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Uncoated Permeable Films Transparent film for adhesive tapes Literature reference: A211 |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic | 0.50 | ||
| vs. Itself - Static | 0.70 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 35 | µm | |
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD : 35 µm | > 3000 | MPa | |
| 1% Secant, TD : 35 µm | > 1500 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 35 µm | 125 | MPa | |
| TD : Yield, 35 µm | 70.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 35 µm | 22 | % | |
| TD : Break, 35 µm | 70 | % | |
| Oxygen Transmission Rate (Wet) (23°C, 35 µm, 0.0% RH) | 1.00 | cm³/m²/24 hr | ASTM F1927 |
| Yield (34.8 µm) | 20.0 | m²/kg | Internal Method |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ferro PP TPP40AD37NA | Ferro Corporation | PP Homopolymer | Ferro PP |
| Karina LILAC 2563U -E TR-600N34/189-YT-AS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Plenco 03356 (Compression) | Plastics Engineering Co. | Phenolic | Plenco |
| Hostacom TRC 787N E1 G71535 | LyondellBasell Industries | PP Copolymer | Hostacom |
| Sylvin 2910-80 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |