Pearlthane® 11T60D
| Category: | TPU-Capro , Thermoplastic Polyurethane Elastomer (Polycaprolactone) |
| Manufacturer: | Lubrizol Advanced Materials, Inc. |
| Trademark: | Pearlthane® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | G5XEmR_Pearlthane-11T60D.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Pearlthane® 11T60D is a polycaprolactone copolyester based TPU, supplied in form of translucent, colourless pellets, combining very high hardness with excellent mechanical properties. It is especially advisable for use in producing technical parts by injection moulding. Pearlthane® 11T60D is especially adequate for the production of shoe heels and top - pieces, rollers, ear-tags, and a variety of injection-moulded components. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.19 | g/cm³ | ASTM D792 |
| 20°C | 1.19 | g/cm³ | ISO 2781 |
| Moisture Content | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion Loss | 25.0 | mm³ | ISO 4649 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 58 | ASTM D2240, ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412, ISO 527 | ||
| 100% strain | 15.0 | MPa | ASTM D412, ISO 527 |
| 300% strain | 28.0 | MPa | ASTM D412, ISO 527 |
| Tensile Strength (Yield) | 40.0 | MPa | ASTM D412, ISO 527 |
| Tensile Elongation (Break) | 480 | % | ASTM D412, ISO 527 |
| Tear Strength | |||
| -- 1 | 170 | kN/m | ASTM D624 |
| -- | 170 | kN/m | ISO 34-1 |
| Compression Set (23°C, 70 hr) | 35 | % | ASTM D395B |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature 2 | -24.0 | °C | ISO 11357-2 |
| Melting Temperature 3 | 202 - 212 | °C | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 110 | °C | |
| Drying Time | 1.0 - 2.0 | hr | |
| Rear Temperature | 210 | °C | |
| Middle Temperature | 215 | °C | |
| Front Temperature | 225 | °C | |
| Nozzle Temperature | 220 | °C | |
| Mold Temperature | 35.0 | °C | |
| Screw L/D Ratio | 23.0:1.0 |
| Injection instructions |
|---|
| Closing force: : 30 tonsScrew diameter: : 30 mmMaximum hydraulic pressure: : 210 barMould: : Plaque 120x120x2 mm |
| Note Message | |
|---|---|
| 1 . | C mould |
| 2 . | 10°C /min |
| 3 . | Temperature at which MFI = 10 g/10 min @ 21.6 kg |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RJM SN601G40AH | RJM International, Inc. | Nylon 66 | RJM |
| Badamid® T70 GF30 | Bada AG | Nylon 6/6T | Badamid® |
| KOPA® KN133G30WH | Kolon Plastics, Inc. | Nylon 6 | KOPA® |
| Plexiglas® Satinice df23 7N | Evonik Industries AG | Acrylic (PMMA) | Plexiglas® |
| XYLEX™ X7507 resin | SABIC Innovative Plastics | PC+Polyester | XYLEX™ |