PETROTHENE LR590001 is designed as primary insulation for telephone singles. LR590001 is a high density resin designed for low shrinkback after extrusion. Antioxidant has been added to ensure thermal stability during processing. The resin also contains a metal deactivator to prevent degradation from copper while the cable is in service. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.948 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.80 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (100% Igepal, Compression Molded, F0) | 48.0 | hr | ASTM D1693 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, Compression Molded | 21.7 | MPa | |
| Break, Compression Molded | 16.2 | MPa | |
| Tensile Elongation (Break, Compression Molded) | 590 | % | ASTM D638 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -76.0 | °C | ASTM D746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+18 | ohms·cm | ASTM D991 |
| Dielectric Constant (1 MHz) | 2.33 | ASTM D1531 | |
| Dissipation Factor (1 MHz) | 7.0E-5 | ASTM D1531 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 149 to 163 | °C | |
| Cylinder Zone 2 Temp. | 177 to 204 | °C | |
| Cylinder Zone 3 Temp. | 204 to 232 | °C | |
| Cylinder Zone 4 Temp. | 246 to 260 | °C | |
| Adapter Temperature | 246 to 260 | °C | |
| Melt Temperature | 246 to 260 | °C | |
| Die Temperature | 246 to 260 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| REPOL® MI3535 | Reliance Industries Limited | PP Impact Copolymer | REPOL® |
| TRAMID® 4110G33 | Samyang Corporation | Nylon, Unspecified | TRAMID® |
| AFLAS® 150P | Asahi Glass Co., Ltd. | Fluorelastomer | AFLAS® |
| Andur 5-DP-LM/Curene® 3005 | Anderson Development Company | PUR-Ester/TDI | Andur |
| NORYL™ N1150 resin | SABIC Innovative Plastics Asia Pacific | PPE+PS | NORYL™ |