DOW™ LDPE 535E
| Category: | LDPE , Low Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOW™ LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | G4F5XP_DOW-LDPE-535E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DOW LDPE 535E is a medium density LDPE with a melt index of 0.6. It is suitable for the processing of shrink films and has a good balance between shrinkage properties (heat shrinkage and cold shrinkage), optical properties such as high gloss and low haze, and mechanical properties. Main features:
EU, No 10/2011 please consult the regulation for complete details. |
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.928 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.60 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | 0.30 - 0.45 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| secant modulus | ASTM D882 | ||
| 2% secant, MD : 50 µm, blown film | 211 | MPa | ASTM D882 |
| 2% secant, TD : 50 µm, blown film | 219 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 50 µm, blown film | 12.0 | MPa | ASTM D882 |
| TD : Yield, 50 µm, blown film | 13.0 | MPa | ASTM D882 |
| MD : Broken, 50 µm, blown film | 22.0 | MPa | ASTM D882 |
| TD : Broken, 50 µm, blown film | 20.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 50 µm, blown film | 370 | % | ASTM D882 |
| TD : Broken, 50 µm, blown film | 530 | % | ASTM D882 |
| Dart Drop Impact (50 µm, Blown Film) | 120 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 50 µm, blown film | 230 | g | ASTM D1922 |
| TD : 50 µm, blown film | 230 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 104 | °C | ASTM D1525 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.0 µm) | 62 | ASTM D2457 | |
| Haze (50.0 µm) | 8.3 | % | ASTM D1003 |
| Extrusion instructions |
|---|
| 吹塑薄膜的制造条件： 放大比：1 比 2.5 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| DURANEX® 303RA | Polyplastics Co., Ltd. | PBT | DURANEX® |
| HiFill® PA6/6 GF33 UV BK001 | Techmer Engineered Solutions | Nylon 66/6 | HiFill® |
| Hylon® N1040MGL | Ravago Manufacturing Americas, LLC | Nylon 66 | Hylon® |
| LNP™ STAT-KON™ DX10315C compound | SABIC Innovative Plastics Asia Pacific | PC | LNP™ STAT-KON™ |
| ALTECH® PC ECO 1000/141 FR IM GY2493-13LS | ALBIS PLASTIC GmbH | PC | ALTECH® PC |