LNP™ LUBRILOY™ DF2041 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRILOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | G3gIxZ_LNPLUBRILOYDF2041compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRILOY* DF2041 is a compound based on Polycarbonate resin containing Flame Retardant, Proprietary Lubricant, Glass Fiber. Added features of this material include: Flame Retardant. Also known as: LNP* LUBRILOY* Compound DF-20 FR ECO Product reorder name: DF2041 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.33 | g/cm³ | ASTM D792 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.20 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.40 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.39 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.18 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.064 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.12 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 6680 | MPa | ASTM D638 |
| -- | 6830 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Fracture | 101 | MPa | ASTM D638 |
| Fracture | 100 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture | 2.2 | % | ASTM D638 |
| Fracture | 2.0 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 6370 | MPa | ASTM D790 |
| -- | 6270 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 153 | MPa | ASTM D790 |
| -- | 149 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.43 | ASTM D3702 Modified | |
| With Self-Static | 0.36 | ASTM D3702 Modified | |
| Wear Factor - Washer | 57.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 150 | J/m | ASTM D256 |
| 23°C 2 | 9.9 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 600 | J/m | ASTM D4812 |
| 23°C 3 | 37 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 11.8 | J | ASTM D3763 |
| -- | 3.19 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 92.8 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 4 | 102 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 249 - 260 | °C | |
| Middle Temperature | 254 - 266 | °C | |
| Front Temperature | 260 - 271 | °C | |
| Processing (Melt) Temp | 254 - 288 | °C | |
| Mold Temperature | 37.8 - 65.6 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 127 HI | RTP Company | PP, Unspecified | RTP |
| SPESIN® KP213G15SIBL | Kolon Plastics, Inc. | PBT | SPESIN® |
| Cawiton® SN990 | Wittenburg B.V. | SEBS | Cawiton® |
| Grivory® GV-5 FWA black 9225 | EMS-GRIVORY | Nylon 66+Nylon 6I/X | Grivory® |
| Karina BLACK PVC COMPOUND -E 950-48/ 4-A-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |