Nivionplast® B R60G NATURALE
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | SO.F.TER. SPA |
| Trademark: | Nivionplast® B |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | G2MYg3_Nivionplast-B-R60G-NATURALE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 60% glass fiber reinforced polyamide 6 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.70 | g/cm³ | ASTM D792 |
| Molding Shrinkage | 0.15 | % | Internal Method |
| Ash Content | 62 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 19000 | MPa | ASTM D638 |
| Tensile Strength (Break) | 200 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.2 | % | ASTM D638 |
| Flexural Modulus | 18500 | MPa | ASTM D790 |
| Flexural Strength | 340 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 160 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 220 | °C | |
| 1.8 MPa, Unannealed | 210 | °C | |
| Peak Melting Temperature | 220 | °C | ASTM D3417 |
| CLTE - Flow | 2.5E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.20 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 250 | °C | |
| Middle Temperature | 270 | °C | |
| Front Temperature | 280 | °C | |
| Mold Temperature | 80.0 to 90.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadrant EPP Nylatron® GSM | Quadrant Engineering Plastic Products | Nylon 6 | Quadrant EPP |
| XYRON™ X1561 | Asahi Kasei Chemicals Corporation | PPE+PS | XYRON™ |
| Bergamid™ BG6000-8034 RS NC001 | PolyOne Corporation | Nylon 6 | Bergamid™ |
| 3M™ Dyneon™ Fluoroelastomer FG 5630Q | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroelastomer |
| EMAC+® SP1358 | Westlake Chemical Corporation | EMA | EMAC+® |