VECTRA® S471
| Category: | LCP , Liquid Crystal Polymer |
| Manufacturer: | Celanese Corporation |
| Trademark: | VECTRA® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | G2BmE3_VECTRA-S471.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
High flow, High Heat resistance, Low Warpage, for Thick Walled (>0.2mm) or thin (<0.2mm)& Thick Walled Parts. Chemical abbreviation according to ISO 1043-1 : LCP Inherently flame retardant UL-Listing V-0 in natural and black at 0.4mm thickness per UL 94 flame testing. Relative-Temperature-Index (RTI) according to UL 746B: electricals 130°C, mechanicals 130°C. UL = Underwriters Laboratories (USA) |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.76 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 0.50 | % | ISO 294-4 |
| Flow direction | 0.20 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 12000 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 120 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 1.4 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 12000 | MPa | ISO 178 |
| Flexural Stress (23°C) | 185 | MPa | ISO 178 |
| Flexural Strain at Break | 2.0 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 10 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 8.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 1.8 MPa, not annealed | 315 | °C | ISO 75-2/A |
| 8.0 MPa, not annealed | 271 | °C | ISO 75-2/C |
| Melting Temperature 1 | 350 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 8.0E-6 | cm/cm/°C | ISO 11359-2 |
| Lateral | 1.7E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+11 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| Relative Permittivity (1 MHz) | 4.00 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 7.0E-3 | IEC 60250 | |
| Comparative Tracking Index | 150 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 - 170 | °C | |
| Drying Time | 6.0 | hr | |
| Hopper Temperature | 20.0 - 40.0 | °C | |
| Rear Temperature | 330 - 350 | °C | |
| Middle Temperature | 340 - 360 | °C | |
| Front Temperature | 345 - 365 | °C | |
| Nozzle Temperature | 355 - 370 | °C | |
| Processing (Melt) Temp | 360 - 375 | °C | |
| Mold Temperature | 80.0 - 120 | °C | |
| Injection Pressure | 50.0 - 150 | MPa | |
| Injection Rate | Moderate | ||
| Holding Pressure | 50.0 - 150 | MPa | |
| Back Pressure | 0.00 - 3.00 | MPa |
| Injection instructions |
|---|
| Manifold Temperature: 355 to 370°CZone 4 Temperature: 355 to 370°CFeed Temperature: 60 to 80°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X4195 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Manner Flexible PVC V897 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| PTS PCA-1010HF | Polymer Technology and Services, LLC | PC+ABS | PTS |
| TAISOX 6634F | Formosa Plastics Corporation | LDPE | TAISOX |
| ELASTOSIL® E 303 | Wacker Chemie AG | Silicone | ELASTOSIL® E |