Milastomer™ M2400NS
| Category: | TPV , Thermoplastic Vulcanizate |
| Manufacturer: | Mitsui Chemicals America, Inc. |
| Trademark: | Milastomer™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | G1nMPY_Milastomer-M2400NS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Milastomer™M2400NS is a thermoplastic vulcanized rubber (TPV) material,. This product is available in North America and is processed by extrusion. Milastomer™Typical application fields of M2400NS are: engineering/industrial accessories |
| General Information | |
|---|---|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.890 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.50 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 5 sec) | 32 | ISO 48 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1(100% Strain) | 6.30 | MPa | ISO 37 |
| Tensile Stress 2(Break) | 11.8 | MPa | ISO 37 |
| Tensile Elongation 3(Break) | 600 | % | ISO 37 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -60.0 | °C | Internal method |
| Additional Information |
|---|
| All tests performed according to Mitsui methods. |
| Note Message | |
|---|---|
| 1 . | 500 mm/min |
| 2 . | 500 mm/min |
| 3 . | 500 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEREZ PA 6.6 7500 GF 35 H | TER HELL PLASTIC GMBH | Nylon 66 | TEREZ PA 6.6 |
| Hifax EKF 212 D | LyondellBasell Industries | PP, Unspecified | Hifax |
| INNOPOL® PP CS 2-4630 FR | Inno-Comp Ltd. | PP Impact Copolymer | INNOPOL® PP |
| LUCITE® SuperTuf™ ST50G6 | Lucite International Inc. | Acrylic (PMMA) | LUCITE® |
| Osterlene® MI-13-1.4 | Osterman & Company | PS (MIPS) | Osterlene® |