Propafilm™ OLP80
| Category: | PP Alloy , Polypropylene Alloy |
| Manufacturer: | Innovia Films Ltd. |
| Trademark: | Propafilm™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | G1KO7E_Propafilm-OLP80.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
High Speed Overwraping Film with Shrink Tightening Properties Biaxially oriented polypropylene (BOPP) film co-extruded on both sides with heat sealable polyolefinic copolymers. GLP80/100 are suitable for use in the tobacco industry for both high speed and display outers where exceptional pack appearance and wrap tightness are required. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage | Internal Method | ||
| Flow : 80°C, 1 min | 3.7 | % | |
| Flow : 120°C, 1 min | 7.0 | % | |
| Across Flow : 80°C, 1 min | 3.5 | % | |
| Across Flow : 120°C, 1 min | 11 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic, Outside/Outside | 0.30 | ||
| vs. Itself - Static, Outside/Outside | 0.40 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Secant Modulus 1 | ASTM D882 | ||
| 1% Secant, MD | 3000 | MPa | |
| 1% Secant, TD | 3600 | MPa | |
| Tensile Strength 2 | ASTM D882 | ||
| MD : Yield | 170 | MPa | |
| TD : Yield | 210 | MPa | |
| Tensile Elongation 3 | ASTM D882 | ||
| MD : Break | 120 | % | |
| TD : Break | 80 | % | |
| Seal Strength 4 | 0.19 | N/mm | Internal Method |
| Seal Initiation Temperature 5 | 110 to 141 | °C | Internal Method |
| Oxygen Permeability (23°C, 0% RH) | 38 | cm³·mm/m²/atm/24 hr | ASTM F1927 |
| Water Vapor Transmission Rate | ASTM F1770 | ||
| 23°C, 85% RH | 0.93 | g/m²/24 hr | |
| 38°C, 90% RH | 6.0 | g/m²/24 hr | |
| Blocking Load 6 | 6.0 | g | Internal Method |
| Film Gauge | 80.0 | Internal Method | |
| Yield | 54.9 | m²/kg | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (20°) | 130 | ASTM D2457 | |
| Haze 7 | 1.3 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 10%/min |
| 2 . | 50%/min |
| 3 . | 50%/min |
| 4 . | 228°F; 1sec; 15lb/in² |
| 5 . | 2secs; 15lb/in² |
| 6 . | 158°F; 200g; 2hrs |
| 7 . | Wide angle, 2.5° |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Telcar® TL-2480F | Teknor Apex Company | TPE | Telcar® |
| TAROMID A 280 R3 | Taro Plast S.p.A. | Nylon 66 | TAROMID A |
| BESTNYL SE35VI02AX | Triesa Plastics | Nylon 66 | BESTNYL |
| Generic LMDPE | Generic | LMDPE | Generic |
| Lucent PA 66-01 | Lucent Polymers, Inc. | Nylon 66 | Lucent PA |