Ebalta AH 140 / LI 20
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Ebalta Kunststoff GmbH |
| Trademark: | Ebalta |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Fzb8z8_Ebalta-AH-140-LI-20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Applications
Properties
|
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Shore Hardness (Shore D) | 84 to 90 | ISO 7619 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 3070 to 3570 | MPa | ISO 178 |
| Flexural Stress | 113 to 133 | MPa | ISO 178 |
| Compressive Stress | 86.0 to 96.0 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 32 to 70 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 88.0 to 94.0 | °C | ISO 75-2/B |
| Glass Transition Temperature | 83.0 | °C | DSC |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Weight: 35 | ||
| Resin | Mix Ratio by Weight: 100 | ||
| Post Cure Time | |||
| 60°C | 4.0 | hr | |
| 80°C | 6.0 | hr | |
| 120°C | 4.0 | hr |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Density (20°C) | 1.09 to 1.15 | g/cm³ | |
| Viscosity (25°C) | 0.53 to 0.68 | Pa·s | |
| Curing Time (20°C) | 16 to 24 | hr | |
| Pot Life 1(20°C) | 18 to 22 | min |
| Note Message | |
|---|---|
| 1 . | 200 g |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 4785 FR | RTP Company | PTT | RTP |
| Prime Polypro™ E-200GP | Prime Polymer Co., Ltd. | PP Homopolymer | Prime Polypro™ |
| Yuyao PA 022MC | Yuyao Tenglong Plastics Co., Ltd. | Nylon 66/6 | Yuyao PA |
| CHEMIGUM® P7400 | Omnova Solutions Inc. | NBR | CHEMIGUM® |
| LUVOCOM® 1105-7794/BL VP | Lehmann & Voss & Co. | PEEK | LUVOCOM® |