Durethan® DP 2801 000000
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | LANXESS Corporation |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FzMdBM_DurethanDP2801000000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 66, non-reinforced, injection molding, halogen free flame retardant |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.14 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 2577 | |||
| Vertical flow direction : 280°C, 2.00mm 1 | 1.2 | -- | % | ISO 2577 |
| Vertical flow direction : 120°C, 4 hours, 2.00mm 2 | 0.11 | -- | % | ISO 2577 |
| Flow direction : 280°C, 2.00mm 3 | 1.1 | -- | % | ISO 2577 |
| Flow direction : 120°C, 4 hours, 2.00mm 4 | 0.42 | -- | % | ISO 2577 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness | 151 | 70.0 | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 3500 | 1400 | MPa | ISO 527-2/1 |
| Tensile Stress | ||||
| Yield, 23°C | 94.0 | 55.0 | MPa | ISO 527-2/50 |
| Fracture, 23°C | 80.0 | 55.0 | MPa | ISO 527-2/5 |
| Tensile Strain | ||||
| Yield, 23°C | 4.2 | 20 | % | ISO 527-2/50 |
| Fracture, 23°C | 11 | 230 | % | ISO 527-2/5 |
| Nominal Tensile Strain at Break (23°C) | 10 | 160 | % | ISO 527-2/50 |
| Flexural Modulus 5(23°C) | 3200 | 1300 | MPa | ISO 178/A |
| Flexural Stress | ISO 178/A | |||
| 3.5% strain, 23°C | 105 | 36.0 | MPa | ISO 178/A |
| 23°C 6 | 127 | 49.0 | MPa | ISO 178/A |
| Flexural Strain at Flexural Strength 7(23°C) | 6.2 | 8.0 | % | ISO 178/A |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Behavior 8(> 1.00 mm) | passed | -- | ISO 3795 |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 66, GFHR, 14-030; ISO 1043-PA FR (30) | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Admissible Residence Time at Tmax | min | ||
| Residual Moisture Content | 0.030 - 0.070 | % | Karl Fisher |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | < 10 | < 10 | kJ/m² | ISO 179/1eA |
| 23°C | < 10 | 15 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 120 | 190 | kJ/m² | ISO 179/1eU |
| 23°C | 110 kJ/m² | No Break | ISO 179/1eU | |
| Notched Izod Impact | ISO 180/1A | |||
| -30°C | < 10 | < 10 | kJ/m² | ISO 180/1A |
| 23°C | < 10 | 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | 110 | 130 | kJ/m² | ISO 180/1U |
| 23°C | 80 kJ/m² | No Break | ISO 180/1U | |
| Multi-Axial Instrumented Impact Energy | ISO 6603-2 | |||
| -30°C | 5.10 | -- | J | ISO 6603-2 |
| 23°C | 13.1 | 27.2 | J | ISO 6603-2 |
| Multi-Axial Instrumented Impact Peak Force | ISO 6603-2 | |||
| -30°C | 2400 | -- | N | ISO 6603-2 |
| 23°C | 3730 | 4630 | N | ISO 6603-2 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 210 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 75.0 | -- | °C | ISO 75-2/A |
| 8.0 MPa, not annealed | 60.0 | -- | °C | ISO 75-2/C |
| Vicat Softening Temperature | > 230 | -- | °C | ISO 306/B120 |
| Ball Pressure Test (249°C) | Pass | -- | IEC 60695-10-2 | |
| Melting Temperature 9 | 265 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow : 23 to 55°C | 7.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C | 9.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Comparative Tracking Index | IEC 60112 | |||
| Solution a | 600 | -- | V | IEC 60112 |
| Solution B 10 | 400 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.750 mm) | V-2 | -- | UL 94 | |
| Glow Wire Flammability Index (1.00 mm) | 960 | -- | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 0.750 mm | 775 | -- | °C | IEC 60695-2-13 |
| 1.50 mm | 775 | -- | °C | IEC 60695-2-13 |
| 3.00 mm | 775 | -- | °C | IEC 60695-2-13 |
| Oxygen Index 11 | 30 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 - 6.0 | hr | |
| Processing (Melt) Temp | 260 - 270 | °C | |
| Mold Temperature | 80.0 - 100 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2mm, 80°C MT, 600 bar |
| 2 . | 60x60x2mm |
| 3 . | 60x60x2mm, 80°C MT, 600 bar |
| 4 . | 60x60x2mm |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2 mm/min |
| 8 . | US-FMVSS302 |
| 9 . | 10°C/min |
| 10 . | Erosion depth: 1.80mm |
| 11 . | Procedure A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEREZ PA 6 7750 T GF 30 | TER HELL PLASTIC GMBH | Nylon 6 | TEREZ PA 6 |
| LG PS 65IHE | LG Chem Ltd. | PS (HIPS) | LG PS |
| LNP™ THERMOCOMP™ QC008 compound | SABIC Innovative Plastics | Nylon 610 | LNP™ THERMOCOMP™ |
| Sylvin 7844-70C Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| 3M™ Dyneon™ Fluoroelastomer FE 5624Q | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroelastomer |