Karina IVORY PVC COMPOUND 853-35/ 1-DY-IS-LMP
| Category: | PVC, Unspecified , Polyvinyl Chloride |
| Manufacturer: | Karina Ind. e Com. de Plásticos Ltda |
| Trademark: | Karina |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Fy49Ks_Karina-IVORY-PVC-COMPOUND-853-35-1-DY-IS-LMP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HEAVY METAL FREE PVC COMPOUND CLASS 70C (PVC/F), RECOMMENDED FOR INSULATION OF ELECTRICAL WIRES AND FLEXIBLE CORDS. ALSO RECOMMENDED FOR EXTRUSION OF COAXIAL CABLES JACKET. |
| General Information | |
|---|---|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 1.39 to 1.45 | g/cm³ | IEC 60811-1-3 |
| Cadmium Content | < 50 | ppm | ASTM D1971 |
| Chromium Content | < 100 | ppm | ASTM D1971 |
| Color | OK | ME 12 | |
| Color a | -1.72 to 1.28 | ME 12 | |
| Color b | 5.77 to 8.77 | ME 12 | |
| Color L | 86.0 to 89.0 | ME 12 | |
| Mercury Content | < 100 | ppm | ASTM D1971 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Bromine Content | < 100 | ppm | IEC 62321 |
| Lead Content | < 100 | ppm | ASTM D1971 |
| Maximum Variation | < 25 | % | IEC 60811-1-2 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 15 sec) | 86 to 90 | NBR 7456 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | > 12.6 | MPa | IEC 60811-1-1 |
| Tensile Strain (Yield) | > 150 | % | IEC 60811-1-1 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2 | > 12.6 | MPa | IEC 60811-1-2 |
| Tensile Elongation 3(Break) | > 150 | % | IEC 60811-1-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity 4 | > 1.0E+14 | ohms·cm | ASTM D257 |
| Note Message | |
|---|---|
| 1 . | 24 hr |
| 2 . | Aged in Air for 168 hr at 100°C |
| 3 . | Aged in Air for 168 hr at 100°C |
| 4 . | 24 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TechnoFin GF30-22 | TechnoCompound GmbH | PP, Unspecified | TechnoFin |
| TECHNYL® C 218 MZ20 V10 BLACK Z | Solvay Engineering Plastics | Nylon 6 | TECHNYL® C |
| apilon 52® A-6505 | API SpA | TPU-Polyester | apilon 52® |
| Karina IVORY PVC COMPOUND -E 500-35/ 1-Y | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| POCAN® KU 2-7503/1 000000 | LANXESS GmbH | PBT | POCAN® |