Hostacom G2 N02 100000
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hostacom |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FwwEa6_Hostacom-G2-N02-100000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Hostacom G2 N02 (black) is a 20% glass fiber reinforced PP homopolymer (coupled). |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/5.0 kg) | 6.0 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 90.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - Secant (23°C) | 4450 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 70.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield, 23°C) | 4.0 | % | ISO 527-2/50 |
| Flexural Modulus (23°C) | 4100 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 11 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 130 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 132 | °C | ISO 306/B50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVAMID® 66/6 GF 30 FRG 5 TS | Plastcom | Nylon 66/6 | SLOVAMID® 66/6 |
| Daelim Po1y® LL-32HF | DAELIM INDUSTRIAL CO., LTD. | LLDPE | Daelim Po1y® |
| CYCOLOY™ CY6110 resin | SABIC Innovative Plastics Europe | PC+ABS | CYCOLOY™ |
| Hipolyene 2703 MS | Zylog Plastalloys | TPO (POE) | Hipolyene |
| Pearlthane® MB-51UV | Lubrizol Advanced Materials, Inc. | TPU, Unspecified | Pearlthane® |