Sevrene® 3500-70A
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Vi-Chem Corporation |
| Trademark: | Sevrene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FvcOVK_Sevrene-3500-70A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sevrene® 3500-70A is a Thermoplastic Elastomer (TPE) material. It is available in North America for extrusion or injection molding. Typical application of Sevrene® 3500-70A: Automotive |
| General Information | |
|---|---|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.940 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 15 sec) | 66 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress - Flow 1(100% Strain) | 2.40 | MPa | ISO 37 |
| Tensile Stress - Flow 2(Yield) | 8.10 | MPa | ISO 37 |
| Tensile Elongation - Flow 3(Break) | 1300 | % | ISO 37 |
| Tear Strength - Flow 4 | 31.8 | kN/m | ASTM D624 |
| Compression Set | ASTM D395 | ||
| 23°C, 168 hr | 25 | % | |
| 100°C, 168 hr | 58 | % |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength 5(80°C, 1008 hr) | 1.0 | % | ASTM D412 |
| Change in Ultimate Elongation 6(80°C, 1008 hr) | -20 | % | ASTM D412 |
| Thermal | Nominal Value | ||
|---|---|---|---|
| Cold Flexibility (-30°C) 7 | Pass |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Fogging 8 | SAE J1756 | ||
| 21°C | 94.5 | ||
| 100°C | 94.5 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Arizona Weathering 9 | 1.15Surface Defects = Pass | SAE J1976 | |
| Florida Weathering 10 | 0.970Surface Defects = Pass | SAE J1976 | |
| Weather Resistance | SAE J1976 | ||
| -- 11 | 1.87Surface Defects = Pass | ||
| -- 12 | 1.56Surface Defects = Pass |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | 46 | mm/min | FMVSS 302 |
| Note Message | |
|---|---|
| 1 . | 500 mm/min |
| 2 . | 500 mm/min |
| 3 . | 500 mm/min |
| 4 . | Die B, 500 mm/min |
| 5 . | After heat aging |
| 6 . | After heat aging |
| 7 . | CLP 463DD-07-01 |
| 8 . | 3 hrs |
| 9 . | 2 years, Delta E |
| 10 . | 2 years, Delta E |
| 11 . | Interior Xenon, 1240 kj/m² , Delta E |
| 12 . | Exterior Xenon Arc, 2500 kj/m², Delta E |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravago Compounds HM-325 (Comp) | Ravago Manufacturing Americas, LLC | HDPE | Ravago Compounds |
| ELITE™ 5401GS | The Dow Chemical Company | EPE | ELITE™ |
| Lifoflex® GB 1050 | Müller Kunststoffe GmbH | SEBS | Lifoflex® |
| Karina BLACK PVC COMPOUND 956-48/1-C-IS (*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ THERMOCOMP™ RF0049S compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |