RTV-2 P-10B
| Category: | Silicone Rubber, RTV-2 , Silicone Rubber, RTV-2 |
| Manufacturer: | Silicones, Inc. |
| Trademark: | RTV-2 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FvAxkh_RTV-2-P-10B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| P-10, P-15 and P-20 RTV silicone rubbers are two-component, platinum-catalyzed systems that cure at room temperature. All of these materials have low viscosity, high elongation, high tear strength and low durometer. They are easy to mix and de-air, and will cure with virtually no shrinkage. The speed at which the rubber hardens can be dramatically accelerated with heat or with Pt Accelerator at room temperature. Addition-cure two-component silicone rubbers exhibit excellent chemical and heat resistance, but may show inhibition sensitivity. P-10, P-15 and P-20 offer excellent release properties and are extremely useful for casting complex shapes, animatronic skins, or any application here exceptional flexibility and tear resistance are required. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Specific Gravity | 1.08 | g/cm³ |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Service Temperature - Cured | -51 to 288 | °C |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coverage - Cured | 0.925 | cm³/g |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Weight: 1.0 Mix Ratio by Volume: 11 | ||
| Resin | Mix Ratio by Weight: 10 Mix Ratio by Volume: 100 | ||
| Shelf Life | 26 | wk | |
| Thermoset Mix Viscosity 1 | 5000 to 15000 | cP |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Color 2 | Translucent | ||
| Viscosity 3 | 10 to 20 | Pa·s | |
| Curing Time | 16 to 18 | hr | |
| Pot Life | 60 to 120 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | |||
| Shore A 4 | 6 to 14 | ||
| Shore A 5 | 8 to 16 | ||
| Tensile Strength | 2.07 to 2.76 | MPa | ASTM D412 |
| Tensile Elongation at Break | 400 to 500 | % | ASTM D412 |
| Tear Strength | 8.76 to 17.5 | kN/m | ASTM D624 |
| Note Message | |
|---|---|
| 1 . | Mixed |
| 2 . | Base |
| 3 . | Base |
| 4 . | 1 Day |
| 5 . | 7 Days |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 128 HF | RTP Company | PP Homopolymer | RTP |
| PRIMALENE WPP111 | Southern Polymer, Inc. | PP Homopolymer | PRIMALENE |
| Hostaform® LU-02XAP® | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| INNOPOL® PP CS 2-9120 | Inno-Comp Ltd. | PP Copolymer | INNOPOL® PP |
| Polifor® L15 MU/40 NATURALE | SO.F.TER. SPA | PP Homopolymer | Polifor® |