Synres-Almoco DAP 5563
| Category: | DAP , Diallyl Phthalate |
| Manufacturer: | Synres-Almoco BV |
| Trademark: | Synres-Almoco |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FuQFwZ_Synres-Almoco-DAP-5563.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Glass-fibre reinforced diallyl phthalate moulding compound Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exceptional dimensional stability even under severe environmental conditions, easy flowing for use in long runner systems. Primary application(s): Connectors, Bobbins, Potentiometers, switches This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/95 (RoHS), 2002/96 (WEEE) and 2006/122 (PFOS) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.80 to 2.00 | g/cm³ | ISO 1183 |
| Apparent Density | 0.75 to 0.90 | g/cm³ | ISO 60 |
| Molding Shrinkage - Flow 1 | 0.15 to 0.45 | % | ISO 2577 |
| Water Absorption (23°C, 24 hr) | < 0.20 | % | ISO 62 |
| Post Shrinkage 2 | < 0.050 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Injection Molded) | 10000 to 14000 | MPa | ISO 527-2 |
| Tensile Stress (Injection Molded) | 80.0 to 90.0 | MPa | ISO 527-2 |
| Flexural Modulus (Injection Molded) | 14000 to 18000 | MPa | ISO 178 |
| Flexural Stress (Injection Molded) | 120 to 160 | MPa | ISO 178 |
| Compressive Stress | 150 to 200 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (Injection Molded) | 3.5 to 4.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (Injection Molded) | 7.0 to 10 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 1.8 MPa, Unannealed | > 200 | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 120 to 140 | °C | ISO 75-2/C |
| CLTE - Flow (50 to 100°C) | 5.0E-6 to 1.0E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.90 to 1.1 | W/m/K | ASTM E1461 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 to 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+14 to 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | 15 to 20 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 5.00 4.50 | ||
| 1 MHz | 4.50 4.00 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 0.010 to 0.030 | ||
| 1 MHz | 0.010 to 0.030 | ||
| Arc Resistance | PLC 4 | ASTM D495 | |
| Comparative Tracking Index | > 500 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-1 | UL 94 | |
| Glow Wire Flammability Index | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | 875 | °C | IEC 60695-2-13 |
| Note Message | |
|---|---|
| 1 . | Injection Molded |
| 2 . | 168 h / 110°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| CABELEC® CA4918 | Cabot Corporation | LDPE | CABELEC® |
| Hifax TRC 835P | LyondellBasell Industries | TPO (POE) | Hifax |
| ICORENE® 1901 | ICO Polymers EMEA, A Division of A. Schulman | Plastomer | ICORENE® |
| LEXAN™ EXL8134 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |
| LUBAN™ 1102 MBF | Oman Oil Refineries & Petroleum Indistries Co. (Orpic) | PP Homopolymer | LUBAN™ |