Safrene® F 7665
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Safripol (PTY) LTD |
| Trademark: | Safrene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FuBXmP_Safrene-F-7665.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Safrene® F 7665 High Density Polyethylene Resin is a medium molecular mass grade with good processing properties. It exhibits a good surface finish with high hardness and rigidity. Safrene® F 7665 High Density Polyethylene Resin is recommended for milk and fruit juice bottles as well as other general purpose bottle applications up to 5 liter where good stiffness is required but environmental stress-crack resistance is not critical. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 0.956 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 0.45 | g/10 min | ISO 1133 |
| 190°C/5.0 kg | 2.0 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Compression Molded) | 64 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/50 | ||
| Yield, molding | 27.0 | MPa | ISO 527-2/50 |
| Fracture, molding | 38.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, Compression Molded) | > 600 | % | ISO 527-2/50 |
| Flexural Stress (3.5% Strain, Compression Molded) | 22.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C, molded | 8.0 | kJ/m² | ISO 179 |
| 23°C, molded | 11 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 77.0 | °C | ISO 306/B |
| Peak Crystallization Temperature (DSC) | 130 - 133 | °C | ISO 3146 |
| Additional Information |
|---|
| Blow Molding conditions: Feed Zone: 160 to 180°C Zone 1: 170 to 190°C Zone 2: 180 to 200°C Zone 3: 180 to 190°C Die: 180 to 190°C Melt Temperature: 180 to 190°C |
| Note Message | |
|---|---|
| 1 . | Unannealed |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makrolon® 2256 | Covestro - Polycarbonates | PC | Makrolon® |
| Rhelon G1833HR-01 | RheTech, Inc. | Nylon 6 | Rhelon |
| UBE Nylon 1015GU6 | UBE Industries, Ltd. | Nylon 6 | UBE Nylon |
| Jamplast JPAH | Jamplast, Inc. | Acetal (POM) Homopolymer | Jamplast |
| LEXAN™ 141R resin | SABIC Innovative Plastics | PC | LEXAN™ |