Kelon® B H CET/30
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Kelon® B |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FtTrGm_Kelon-B-H-CET-30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Compound based on Polyamide 6 (PA 6). Heat stabilised. Mineral filler. Product UL certified. Very high dimensional stability. Good elongation. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.38 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.40 to 0.65 | % | |
| Flow : 2.00 mm | 0.35 to 0.60 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 6500 | MPa | |
| 60°C | 4200 | MPa | |
| 90°C | 2200 | MPa | |
| 120°C | 1700 | MPa | |
| 150°C | 1500 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Break, 23°C | 70.0 | MPa | |
| Break, 60°C | 55.0 | MPa | |
| Break, 90°C | 30.0 | MPa | |
| Break, 120°C | 22.0 | MPa | |
| Break, 150°C | 20.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Break, 23°C | 2.5 | % | |
| Break, 60°C | 3.8 | % | |
| Break, 90°C | 9.0 | % | |
| Break, 120°C | 18 | % | |
| Break, 150°C | 30 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 35 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C, 3.20 mm) | 35 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 210 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 155 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 125 | °C | |
| Vicat Softening Temperature | 200 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 3.0E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | HB | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 240 to 290 | °C | |
| Mold Temperature | 80.0 to 100 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| 2 . | 20,000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SZF4809C | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| Niuk 20GP20 | Shanghai Niuk New Plastic Technology Co., Ltd. | ABS | Niuk |
| Chemical Resources LLD100929 | Chemical Resources, Inc. | LLDPE | Chemical Resources |
| GELOY™ EXGY0071 resin | SABIC Innovative Plastics | ASA | GELOY™ |
| KOPA® KN332G25V0BK | Kolon Plastics, Inc. | Nylon 66 | KOPA® |