LNP™ THERMOCOMP™ KF006XXC compound
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FsIWKg_LNP-THERMOCOMP-KF006XXC-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP KF006XXC is a compound based on Acetal Copolymer resin containing 30% Glass Fiber. Also known as: LNP* THERMOCOMP* Compound KF-1006 Product reorder name: KF006XXC |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.64 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.50 | % | ASTM D955 |
| Across Flow : 24 hr | 1.6 | % | ASTM D955, ISO 294-4 |
| Flow : 24 hr | 0.49 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.20 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 11000 | MPa | ASTM D638 |
| -- | 10400 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 116 | MPa | ASTM D638 |
| Yield | 121 | MPa | ISO 527-2 |
| Break | 116 | MPa | ASTM D638 |
| Break | 121 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 2.0 | % | ASTM D638 |
| Yield | 2.1 | % | ISO 527-2 |
| Break | 2.0 | % | ASTM D638 |
| Break | 2.1 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 9650 | MPa | ASTM D790 |
| -- | 9000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 172 | MPa | ASTM D790 |
| -- | 176 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 53 | J/m | ASTM D256 |
| 23°C 2 | 7.1 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 640 | J/m | ASTM D4812 |
| 23°C 3 | 41 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 8.30 | J | ASTM D3763 |
| -- | 3.30 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 163 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 4 | 164 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 162 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 5 | 161 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 8.3E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 8.2E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 3.6E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 3.7E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 177 to 188 | °C | |
| Middle Temperature | 193 to 204 | °C | |
| Front Temperature | 210 to 221 | °C | |
| Processing (Melt) Temp | 199 to 216 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Siveras™ LX70T40F | Toray Resin Company | LCP | Siveras™ |
| ALAMID® 6.6 GF 30 H | LEIS Polytechnik - polymere Werkstoffe GmbH | Nylon 66 | ALAMID® |
| Idealis 500 | Braskem | HMWPE | Idealis |
| Karina WHITE PVC COMPOUND 851-10/152-E-IS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ VERTON™ MV007SUP compound | SABIC Innovative Plastics Europe | PP, Unspecified | LNP™ VERTON™ |