Thermovin™ 180
| Category: | PVC, Rigid , Rigid Polyvinyl Chloride |
| Manufacturer: | Vi-Chem Corporation |
| Trademark: | Thermovin™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Fs7SRu_Thermovin-180.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Thermovin™ 180 is a Rigid Polyvinyl Chloride material filled with 5.0% filler. It is available in North America for extrusion. Typical application of Thermovin™ 180: Automotive |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 15 sec) | 76 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 49.0 | MPa | ASTM D638 |
| Flexural Modulus - Tangent 2(50.0 mm Span) | 2100 | MPa | ASTM D790 |
| Flexural Strength | 74.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 470 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 87.0 | °C | |
| 1.8 MPa, Unannealed | 80.7 | °C |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Fungal Resistance | Pass | GM 9328P | |
| High Temperature Humidity Resistance | Pass | GM 9329P | |
| Low Temperature Flexibility (-30°C) 3 | No Cracks | GM 9503P | |
| Mixed Fungal Resistance | Pass | GM 9303P | |
| Volatile Loss | 0.21 | % | ASTM D1203 |
| Weather Resistance 4 | SAE J1976 | ||
| Color Change, Delta E | 1.75 | ||
| Surface Defects | Pass | ||
| Xenon Arc 5 | |||
| Color Change, Delta E | 0.500 | ||
| Surface Defects | Pass |
| Note Message | |
|---|---|
| 1 . | Type IV, 500 mm/min |
| 2 . | Method I (3 point load), 1.3 mm/min |
| 3 . | 2 in Mandrel |
| 4 . | 2 yr, Florida, 5° South Direct |
| 5 . | 2500 kJ/m² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SOLPLAST TC 3000B | UTEKSOL d.o.o. | SBS | SOLPLAST TC |
| Alkatuff® LL0228 | Qenos Pty Ltd | LLDPE | Alkatuff® |
| Cevian® K160 | PlastxWorld Inc. | Acrylic, Unspecified | Cevian® |
| Hostacom BA753AC | LyondellBasell Industries | PP Copolymer | Hostacom |
| LinGen FR190 | Shanghai Lin Gen Rubber Materials Co., Ltd. | PPE | LinGen |