TECHNYL® C 52G4 MZ25 GREY R7035
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® C |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FrsLXZ_TECHNYL-C-52G4-MZ25-GREY-R7035.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TECHNYL® C 52G4 MZ25 Grey R7035 is a 25% mineral reinforced melamine cyanurate flame retarded polyamide 6.This product is heat stabilised and is suitable for injection moulding. This product is available in both dark and light electrical Grey, other color |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.37 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (275°C/2.16 kg) | 20 | g/10 min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Across Flow | 0.80 | % | |
| Flow | 0.80 | % | |
| Water Absorption (23°C, 24 hr) | 1.0 | % | ISO 62 |
| Molding Shrinkage Isotropy | 1.00 | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6400 | MPa | ISO 527-2/1A |
| Tensile Strength (Break) | 75.0 | MPa | ASTM D638, ISO 527-2/1A |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638, ISO 527-2/1A |
| Flexural Modulus | |||
| -- | 5700 | MPa | ASTM D790 |
| -- | 6000 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 136 | MPa | ISO 178 |
| Break | 130 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 47 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 55 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 205 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 145 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 130 | °C | ISO 75-2/Af |
| Melting Temperature | 222 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (Solution A) | 525 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | V-2 | ||
| 1.60 mm | V-2 | ||
| 3.20 mm | V-2 | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 0.800 mm | 960 | °C | |
| 1.60 mm | 960 | °C | |
| Oxygen Index | 31 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 230 to 235 | °C | |
| Middle Temperature | 235 to 245 | °C | |
| Front Temperature | 245 to 250 | °C | |
| Mold Temperature | 70.0 to 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shin-Etsu Elastomer KEG-2001-70A/B | Shin-Etsu Silicones of America | Silicone Rubber, HTV | Shin-Etsu Elastomer |
| Ultramid® N-276 NF3001 | BASF Corporation | Nylon 66 | Ultramid® |
| Di-Pak™ E-4701-5 | Hapco Inc. | TP, Unspecified | Di-Pak™ |
| Hapflex™ 781 | Hapco Inc. | TP, Unspecified | Hapflex™ |
| apilon 52® D1 58 | API SpA | TPU-Polyester | apilon 52® |