Celanex® XFR 6842 GF30
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Celanese Corporation |
| Trademark: | Celanex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FrEWlZ_Celanex-XFR-6842-GF30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Celanex XFR 6842 GF30 is a halogen and antimony free flame retardant (V-0 @ 0.4 mm) 30% glass reinforced PBT grade with good processability and no corrosive emissions during processing. It is suitable for parts requiring enhanced tracking resistance, toughness, and flame retardancy at <0.75 mm wall thickness. The product is WEEE and RoHS compliant. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.53 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (250°C/5.0 kg) | 18.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.80 to 1.0 | % | |
| Flow | 0.30 to 0.50 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 83 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9800 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 102 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 2.1 | % | ISO 527-2/1A/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.9 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 35 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength (23°C) | 7.4 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 203 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 207 | °C | ISO 306/B50 |
| Melting Temperature 1 | 225 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 4.0E+16 | ohms | IEC 60093 |
| Volume Resistivity | 2.0E+16 | ohms·cm | IEC 60093 |
| Relative Permittivity (1 MHz) | 3.60 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.014 | IEC 60250 | |
| Comparative Tracking Index | 525 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.400 mm) | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| CYCOLAC™ MGABS02 resin | SABIC Innovative Plastics | ABS | CYCOLAC™ |
| Edgetek™ AT-30GB/000 BK006 | PolyOne Corporation | Acetal (POM) Copolymer | Edgetek™ |
| Karina IVORY PVC COMPOUND -E 832-35/ 1-Y-ERA-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Plenco 01581 (Transfer) | Plastics Engineering Co. | Polyester, TS | Plenco |
| NORYL GTX™ GTX951W resin | SABIC Innovative Plastics Asia Pacific | PPE+PS+Nylon | NORYL GTX™ |