PETLIN LD C225Y
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | PETLIN (MALAYSIA) SDN BHD |
| Trademark: | PETLIN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Fqlxzi_PETLIN-LD-C225Y.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PETLIN LD C225Y is a low density polyethylene resin for high clarity general purpose film applications. It is produced by the state-of-the-art DSM Stamicarbon tubular process. It contains antioxidant (BHT free), slip and antiblock additives. It is intended primarily for blown film process. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.921 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 25 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | 0.10 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Film Thickness - Recommended / Available | 20 to 100 µm | ||
| Tensile Modulus | ISO 527-3 | ||
| MD : 25 µm | 215 | MPa | |
| TD : 25 µm | 232 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Break, 25 µm | 29.5 | MPa | |
| TD : Break, 25 µm | 16.5 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 25 µm | 120 | % | |
| TD : Break, 25 µm | 620 | % | |
| Dart Drop Impact (25 µm) | 83 | g | ASTM D1709 |
| Elmendorf Tear Strength | ISO 6383-2 | ||
| MD : 25 µm | 80000 | N | |
| TD : 25 µm | 30000 | N |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.0 µm) | 63 | ASTM D2457 | |
| Haze (25.0 µm) | 7.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 150 to 170 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® LDF 702-T | Marco Polo International, Inc. | LDPE | MARPOL® |
| Sylvin 9468-65 Black | Sylvin Technologies Incorporated | PVC+NBR | Sylvin |
| Badadur® PBT8 GF30 TM-Z2 | Bada AG | PBT | Badadur® |
| Hypro® PPC-GF20 NATURAL | Entec Polymers | PP Impact Copolymer | Hypro® |
| LNP™ STAT-KON™ SX90398 compound | SABIC Innovative Plastics | Nylon 12 | LNP™ STAT-KON™ |