Ultramid® 8202 HS
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FpkTPp_Ultramid-8202-HS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultramid 8202 HS is a heat stabilized, low viscosity, general purpose PA6 injection molding. It possesses the combination of strength and toughness and has excellent chemical and abrasion resistance. The heat stabilizer system extends the retention of properties at the more elevated temperatures. Excellent in filling thin walls or areas. Applications Ultramid 8202 HS is generally recommended for drapery hardware, gears, fittings, furniture casters, bearings, handles, clips, fasteners and thin parts. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.13 | -- | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage - Flow (3.18 mm) | 1.2 | -- | % | |
| Water Absorption | ||||
| 24 hr | 1.6 | -- | % | ASTM D570 |
| 23°C, 24 hr | 1.6 | -- | % | ISO 62 |
| Saturation | 9.5 | -- | % | ASTM D570 |
| Saturation, 23°C | 9.5 | -- | % | ISO 62 |
| Equilibrium, 50% RH | 2.7 | -- | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 2.7 | -- | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 119 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | ISO 527-2 | |||
| 23°C | 2700 | 970 | MPa | |
| 80°C | 485 | 550 | MPa | |
| 121°C | 360 | 320 | MPa | |
| Tensile Strength | ||||
| Yield, -40°C | 126 | 110 | MPa | ASTM D638, ISO 527-2 |
| Yield, 23°C | 79.0 | 36.0 | MPa | ASTM D638 |
| Yield, 80°C | 35.0 | 30.0 | MPa | ASTM D638, ISO 527-2 |
| Yield, 121°C | 25.0 | 20.0 | MPa | ASTM D638, ISO 527-2 |
| Yield, 23°C | 78.0 | 36.0 | MPa | ISO 527-2 |
| Break, 23°C | 75.0 | 60.0 | MPa | ASTM D638 |
| Tensile Elongation | ||||
| Yield, 23°C | 4.0 | 16 | % | ASTM D638, ISO 527-2 |
| Yield, 80°C | 42 | 35 | % | ASTM D638 |
| Yield, 121°C | 36 | 40 | % | ASTM D638 |
| Break, 23°C | 55 | > 100 | % | ASTM D638 |
| Nominal Tensile Strain at Break (23°C) | 25 | > 50 | % | ISO 527-2 |
| Flexural Modulus | ||||
| -40°C | 3010 | 3660 | MPa | ASTM D790 |
| 23°C | 2830 | 740 | MPa | ASTM D790 |
| 65°C | 500 | -- | MPa | ASTM D790 |
| 90°C | 350 | -- | MPa | ASTM D790 |
| 121°C | 305 | -- | MPa | ASTM D790 |
| 23°C | 2400 | 770 | MPa | ISO 178 |
| Flexural Strength | ||||
| -40°C | 170 | 154 | MPa | ASTM D790 |
| 23°C | 108 | 35.0 | MPa | ASTM D790 |
| 65°C | 30.0 | -- | MPa | ASTM D790 |
| 90°C | 20.0 | -- | MPa | ASTM D790 |
| 121°C | 17.0 | -- | MPa | ASTM D790 |
| 23°C | 85.0 | 25.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.5 | -- | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | ISO 179 | |||
| -30°C | 51 | -- | kJ/m² | |
| 23°C | No Break | -- | ||
| Notched Izod Impact | ASTM D256 | |||
| -40°C | 48 | 43 | J/m | |
| 23°C | 58 J/m | No Break | ||
| Drop Impact Resistance (23°C) | 142 | > 271 | J | Internal Method |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ||||
| 0.45 MPa, Unannealed | 178 | -- | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 65.0 | -- | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 60.0 | -- | °C | ISO 75-2/A |
| Peak Melting Temperature | 220 | -- | °C | ASTM D3418, ISO 3146 |
| CLTE - Flow | 8.3E-5 | -- | cm/cm/°C | ASTM E831 |
| RTI Elec | UL 746 | |||
| 0.710 mm | 130 | -- | °C | |
| 1.50 mm | 130 | -- | °C | |
| 3.00 mm | 130 | -- | °C | |
| 6.00 mm | 130 | -- | °C | |
| RTI Imp | UL 746 | |||
| 0.710 mm | 95.0 | -- | °C | |
| 1.50 mm | 105 | -- | °C | |
| 3.00 mm | 105 | -- | °C | |
| 6.00 mm | 105 | -- | °C | |
| RTI Str | UL 746 | |||
| 0.710 mm | 95.0 | -- | °C | |
| 1.50 mm | 105 | -- | °C | |
| 3.00 mm | 105 | -- | °C | |
| 6.00 mm | 105 | -- | °C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | ||||
| 1.50 mm | > 1.0E+13 | -- | ohms·cm | ASTM D257 |
| -- | > 1.0E+13 | -- | ohms·cm | IEC 60093 |
| Dielectric Strength | ||||
| 1.50 mm 1 | 22 | -- | kV/mm | ASTM D149 |
| -- | 37 | -- | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.710 mm | V-2 | -- | ||
| 1.50 mm | V-2 | -- | ||
| 3.00 mm | V-2 | -- | ||
| 6.00 mm | V-2 | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 240 to 285 | °C | |
| Mold Temperature | 65.0 to 80.0 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast |
| Note Message | |
|---|---|
| 1 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRANSMARE® 10HT20-0.001 | Transmare Compounding B.V. | PP Homopolymer | TRANSMARE® |
| Multi-Flam™ 2903 | Multibase, A Dow Corning Company | LDPE | Multi-Flam™ |
| ALFATER XL® A70E 2GP0000 | ALBIS PLASTIC GmbH | TPV | ALFATER XL® |
| Ferro PP TPP10AN84BK | Ferro Corporation | PP, Unspecified | Ferro PP |
| LEXAN™ EXL9330 resin | SABIC Innovative Plastics | PC | LEXAN™ |