TECHNYL® 2411GF6 Bright
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FpIOC9_TECHNYL-2411GF6-Bright.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 66, 30% glass fiber reinforced, for injection molding |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.38 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | |||
| Across Flow | 0.80 | -- | % | |
| Flow | 0.50 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.80 | -- | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 121 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength (Yield) | 1950 | -- | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.0 | -- | % | ASTM D638 |
| Flexural Modulus | 9100 | -- | MPa | ASTM D790 |
| Flexural Strength (Break) | 270 | -- | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | 120 | -- | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 255 | -- | °C | ASTM D648 |
| Melting Temperature | 262 | -- | °C | ISO 11357-3 |
| CLTE - Flow (23 to 85°C) | 2.5E-5 | -- | cm/cm/°C | ASTM D696 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 6.0E+14 | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength | 3.8 | 4.0 | kV/mm | IEC 60243-1 |
| Relative Permittivity | 40.0 | 30.0 | IEC 60250 | |
| Dissipation Factor | 0.010 | 0.11 | IEC 60250 | |
| Comparative Tracking Index | IEC 60112 | |||
| Solution A | 600 | 600 | V | |
| Solution B | 500 | 500 | V |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 to 3.20 mm) | HB | -- | UL 94 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| -- | 650 | -- | °C | |
| 0.800 mm | 650 | -- | °C | |
| Glow Wire Ignition Temperature (1.60 mm) | 650 | -- | °C | IEC 60695-2-13 |
| Oxygen Index | 23 | -- | % | ISO 4589-2 |
| Fire and Smoke F Index - I2, F3 | 2 | -- | NF F16-101 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 270 to 275 | °C | |
| Middle Temperature | 275 to 285 | °C | |
| Front Temperature | 285 to 295 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TITANLENE® LDF 606GG | Lotte Chemical Titan (M) Sdn. Bhd. | LDPE | TITANLENE® |
| U-polymer C300VN | UNITIKA Plastics Division | Polyarylate | U-polymer |
| Geon™ Vinyl Flexible B5DW2 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| ISOTHANE® 3095A | Great Eastern Resins Industrial Co Ltd (GRECO) | TPU-Polyether | ISOTHANE® |
| DuPure® QW 76 AV | Ducor Petrochemicals BV | PP Random Copolymer | DuPure® |