Boda BDT651P
| Category: | Fluorelastomer , Fluoroelastomer |
| Manufacturer: | Chenguang Fluoro & Silicone Elastomers Co., Ltd. |
| Trademark: | Boda |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Fp4ZEF_Boda-BDT651P.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
BDT651P is a high viscosity curative incorporated fluoroelastomer terpolymer. This grade is well suited for application where good hot tear resistance, metal bonding properties and superior fluid resistance than copolymers are required. BDT651P can be compounded to meet the major fluoroelastomer specifications. BDT651P can be used for compression molding of oil seals and complicated geometries. It can be mixed using typical fluoroelastomer compounding ingredients. Mixing can be accomplished with two-roll mills or internal mixers. Finished goods can be produced by a variety of rubber processing methods. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.86 | g/cm³ | |
| Mooney Viscosity (ML 1+10, 121°C) | 60 | MU | |
| Fluorine Content | 68 | % | |
| Solubility | LMW Ketones and esters |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| MH 1(177°C) | 2.45 | N·m | |
| ML 2(177°C) | 0.500 | N·m | |
| t'90 3(177°C) | 2.9 | min | |
| ts2 4(177°C) | 2.9 | min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness 5(Shore A) | 77 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 6(Yield) | 13.6 | MPa | ASTM D412 |
| Tensile Elongation 7(Break) | 270 | % | ASTM D412 |
| Compression Set (200°C, 70 hr) | 31 | % | ASTM D395B |
| Additional Information |
|---|
| Test Compound: Polymer: 100 MT Black (N990): 30 phr MgO: 3 phr Ca(OH)2: 6 phr Curing Condition: Press: 10 min at 170°C Oven: 24 hr at 230°C |
| Note Message | |
|---|---|
| 1 . | MDR2000 Rheometer, 100cpm, 0.5° Arc, 6 minutes |
| 2 . | MDR2000 Rheometer, 100cpm, 0.5° Arc, 6 minutes |
| 3 . | MDR2000 Rheometer, 100cpm, 0.5° Arc, 6 minutes |
| 4 . | MDR2000 Rheometer, 100cpm, 0.5° Arc, 6 minutes |
| 5 . | Press Time: 10 min, Press Temperature: 170°C, Post Cure Time: 24 hr, Post Cure Temperature: 230°C |
| 6 . | Press Time: 10 min, Press Temperature: 170°C, Post Cure Time: 24 hr, Post Cure Temperature: 230°C |
| 7 . | Press Time: 10 min, Press Temperature: 170°C, Post Cure Time: 24 hr, Post Cure Temperature: 230°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TIPPLEN® R 780 | MOL Petrochemicals Co. Ltd. | PP Random Copolymer | TIPPLEN® |
| Baytec® 33965-1 | Covestro - PUR | TSU | Baytec® |
| ColorFast® PBA1000 | LTL Color Compounders, Inc. | ABS+PBT | ColorFast® |
| Desmovit® DP LFC 9350 | geba Kunststoffcompounds GmbH | TPU-Polyether | Desmovit® |
| FHR Polypropylene P4C6B-134A | Flint Hills Resources, LP | PP Homopolymer | FHR Polypropylene |