LNP™ LUBRICOMP™ FX86496 compound
| Category: | PE, Unspecified , Polyethylene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FowDAU_LNP-LUBRICOMP-FX86496-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* LUBRICOMP* FX86496 is a compound based on Polyethylene containing Proprietary Filler(s). Added feature of this grade is: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound PDX-F-86496 Product reorder name: FX86496 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hours | 1.7 | % | ASTM D955 |
| Transverse flow : 24 hours | 1.9 | % | ASTM D955 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.020 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.010 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 594 | MPa | ASTM D638 |
| -- | 423 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 9.00 | MPa | ASTM D638 |
| Yield | 9.00 | MPa | ISO 527-2/5 |
| Fracture 3 | 9.00 | MPa | ASTM D638 |
| Fracture | 9.00 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 10 | % | ASTM D638 |
| Yield | 9.9 | % | ISO 527-2/5 |
| Fracture 5 | 22 | % | ASTM D638 |
| Fracture | 20 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0mm span 6 | 408 | MPa | ASTM D790 |
| -- 7 | 284 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 9.70 | MPa | ISO 178 |
| Yield, 50.0mm span 8 | 9.00 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 39 | J/m | ASTM D256 |
| 23°C 9 | 3.4 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 470 | J/m | ASTM D4812 |
| 23°C 10 | 49 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 58.0 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 11 | 51.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 45.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 12 | 40.0 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ASTM D696 | ||
| Flow : -30 to 30°C | 1.8E-4 | cm/cm/°C | ASTM D696 |
| Lateral : -30 to 30°C | 1.7E-4 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 193 - 204 | °C | |
| Middle Temperature | 210 - 221 | °C | |
| Front Temperature | 221 - 232 | °C | |
| Processing (Melt) Temp | 232 | °C | |
| Mold Temperature | 37.8 - 54.4 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | Type 1, 5.0 mm/min |
| 5 . | Type 1, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 mm |
| 12 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene T20P250-00 | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| Sumitomo DAP FS-10-VO-200-P | Sumitomo Bakelite North America, Inc. | DAP | Sumitomo DAP |
| WPP PP PPH3TF2-Natural | Washington Penn Plastic Co. Inc. | PP Homopolymer | WPP PP |
| Chemlon® 100 W | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |
| KPOL-PP K-PPC 6.0 | KPOL Chem Co. | PP Impact Copolymer | KPOL-PP |