Modified Plastics MPP-S1
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Modified Plastics, Inc. |
| Trademark: | Modified Plastics |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Fnuqk0_Modified-Plastics-MPP-S1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Modified Plastics MPP-S1 is a Polypropylene product. It can be processed by injection molding and is available in North America. Primary characteristic: moisture resistant. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.908 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 1.5 | % | ASTM D955 |
| Water Absorption (24 hr) | 5.0E-3 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 34.5 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 10 | % | ASTM D638 |
| Flexural Strength (Yield) | 48.3 | MPa | ASTM D790 |
| Compressive Strength | 46.9 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 6.35 mm) | 21 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C, 6.35 mm) | 850 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 118 | °C | |
| 1.8 MPa, Unannealed | 98.9 | °C | |
| CLTE - Flow | 6.8E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.12 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength | 26 | kV/mm | ASTM D149 |
| Dielectric Constant | 2.25 | ASTM D150 | |
| Dissipation Factor | 2.0E-4 | ASTM D150 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Processing (Melt) Temp | 163 | °C | |
| Mold Temperature | 32.2 to 65.6 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P3880 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| RTP 207E | RTP Company | Nylon, Unspecified | RTP |
| Nypol® PA A3 G33 HS NTLA013 NR307 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Formolene® 6510A | Formosa Plastics Corporation, U.S.A. | PP Impact Copolymer | Formolene® |
| Lifocork® TO 751004-4 | ELASTO | EVA | Lifocork® |