Pexidan® H/T
| Category: | XLPE , Crosslinked Polyethylene |
| Manufacturer: | Saco Polymers |
| Trademark: | Pexidan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Fmxpd9_Pexidan-H-T.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Low density moisture curable polyethylene compound for 125°C/150°C appliance wire and 125°C coil-lead applications. Pexidan® H/T is a low density XLPE system curable by moisture and consists of a silane pre-grafted base compound A-3001 and a flame-retardant catalyst masterbatch CAT-012FR (Sioplas method). Mixed in the proper proportions (67/33) the two components result, after extrusion, in a material curable by exposure to hot water at 70-90°C or even ambient moisture. Pexida n® H/T is listed with CSA for AWM and CL-1251/1252 and is suitable for UL AWM styles 3173 and 3321. See below for a more complete list of suitable AWM styles. Pexidan® H/T is a RoHS-compliant system. In addition to common AWM styles 3173 and 3321, Pexidan® H/T is suitable for the following AWM XLPE styles: 3176, 3168, 3182, 3194, 3195, 3196, 3199, 3289, 3290, 3295, 3296, 3297, 3298, 3300, 3343, 3344, and 3578 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.08 | g/cm³ | ASTM D792 |
| Degree of Crosslinking | 68 | % | ASTM D2765 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deformation | 10 | % | UL 758 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame test- Horizontal | Pass | CSA FT-2 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Hot Elongation - elongation under load 1(150°C) | 45 | % | Internal method |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Head Temperature | 185 | °C | |
| Screw cooling | neutral |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Fracture 2 | 15.2 | MPa | CSA 22.2 No. 210.2 |
| Fracture | 15.9 | MPa | CSA 22.2 No. 210.2 |
| Tensile Elongation 3(Break) | 300 | % | CSA 22.2 No. 210.2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -50.0 | °C | ASTM D746 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Curing can be done in the following ways: by immersion in hot water at 90-95°C by exposure to low pressure steam ambient atmospheric moisture In all cases curing time depends on wall thickness, temperature, relative humidity and quantity of wire on the reel.Typical values reported above (except MFR) are obtained from 20 AWG wire with wall thickness of 0.015", cured in hot water (6 hours @ 95°C). |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 154 - 171 | °C | |
| Cylinder Zone 2 Temp. | 154 - 171 | °C | |
| Cylinder Zone 3 Temp. | 154 - 171 | °C | |
| Cylinder Zone 4 Temp. | 154 - 171 | °C | |
| Die Temperature | 185 | °C |
| Note Message | |
|---|---|
| 1 . | 15 minutes, 0.2 N/mm² load |
| 2 . | After thermal ageing (7days @180°C) |
| 3 . | After thermal ageing (7days @180°C) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom SC8F-2088 | Spartech Polycom | PPE+PS | Spartech |
| VESTAMID® Terra DS18-GF30 | Evonik Industries AG | Nylon 1010 | VESTAMID® Terra |
| YUNTIANHUA® SF-10 | YunNan YunTianHua Co., Ltd. | Acetal (POM) Copolymer | YUNTIANHUA® |
| Karina IVORY PVC COMP. -E 105852-35/ 1-A-IS-L | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| TABOREX® TA 1137 MD | SILON s.r.o. | MDPE | TABOREX® |