Kingfa GFPP-L40
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Kingfa |
| Trademark: | Kingfa |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Fme9n5_Kingfa-GFPP-L40.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Kingfa GFPP-L40 is a polypropylene material containing 40% long glass fibers. This product is available in the Asia-Pacific region and is processed by injection molding. The main features of Kingfa GFPP-L40 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.22 | g/cm³ | ISO 1183 |
| Spiral Flow 1 | 60.0 | cm | |
| Molding Shrinkage | Internal method | ||
| Vertical flow direction | 0.20 | % | Internal method |
| Flow direction | 0.10 | % | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 112 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 118 | MPa | ISO 527-2/10 |
| Tensile Strain (Break) | 2.5 | % | ISO 527-2/10 |
| Flexural Modulus 2 | 7400 | MPa | ISO 178 |
| Flexural Stress 3 | 168 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 37 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, unannealed, 4.00mm span | 162 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 157 | °C | ISO 75-2/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.20 mm) | HB | UL 94 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Fiber Length | 1.00 - 1.20 | cm | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 90.0 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 210 - 230 | °C | |
| Middle Temperature | 240 - 260 | °C | |
| Front Temperature | 220 - 240 | °C | |
| Processing (Melt) Temp | 230 - 250 | °C | |
| Mold Temperature | 30.0 - 60.0 | °C | |
| Injection Rate | Moderate-Fast |
| Injection instructions |
|---|
| Processing Temp. Limit: 270°C |
| Note Message | |
|---|---|
| 1 . | Melt temperature: 250°C |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MAZMID B 150 FV20 EV10 | Mazzaferro Indústria e Comércio de Polímeros e Fibras Ltda. | Nylon 6 | MAZMID B |
| Axiall PVC 12881 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| PHOENIX™ 6301 | Phon Tech Industrial Company | TPE | PHOENIX™ |
| Plexiglas® LED white 0V606 | Evonik Industries AG | Acrylic (PMMA) | Plexiglas® |
| Hostacom CR 250 F/M C11462 | LyondellBasell Industries | PP Copolymer | Hostacom |