TRANSMARE® BIO 6LA-3CE00
| Category: | PLA , Polylactic Acid |
| Manufacturer: | Transmare Compounding B.V. |
| Trademark: | TRANSMARE® BIO |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FlrgBX_TRANSMARE-BIO-6LA-3CE00.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TRANSMARE® BIO 6LA-3CE00 is a chain extended PLA INGEO™ based biopolymer. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.25 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.0 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Injection Molded) | 80 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C, 4.00 mm, Injection Molded) | 3600 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield, 4.00mm, injection molding | 72.0 | MPa | ISO 527-2/50 |
| Fracture, 4.00mm, injection molding | 60.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield, 4.00mm, injection molding | 2.4 | % | ISO 527-2/50 |
| Fracture, 4.00mm, injection molding | 5.8 | % | ISO 527-2/50 |
| Flexural Modulus (Injection Molded) | 3100 | MPa | ISO 178 |
| Flexural Stress (Injection Molded) | 102 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1A | ||
| -40°C, injection molding | 2.6 | kJ/m² | ISO 179/1A |
| 23°C, injection molding | 2.4 | kJ/m² | ISO 179/1A |
| Charpy Unnotched Impact Strength | ISO 179/1U | ||
| -40°C, injection molding | 23 | kJ/m² | ISO 179/1U |
| 23°C, injection molding | 20 | kJ/m² | ISO 179/1U |
| Notched Izod Impact | ISO 180/1A | ||
| -40°C, injection molding | 2.8 | kJ/m² | ISO 180/1A |
| 23°C, injection molding | 2.9 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -40°C, injection molding | 20 | kJ/m² | ISO 180/1U |
| 23°C, injection molding | 17 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 52.0 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 50.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 58.0 | °C | ISO 306/A |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 165 | °C | |
| Middle Temperature | 185 | °C | |
| Front Temperature | 195 | °C | |
| Nozzle Temperature | 205 | °C | |
| Mold Temperature | 25.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| In specific cases pre-drying of this material might be required. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravamid® R210 T53 | Ravago Group | Nylon 66 | Ravamid® |
| Chemical Resources LD38921 | Chemical Resources, Inc. | LDPE | Chemical Resources |
| Luxus PP 16138 | Luxus Limited | PP, Unspecified | Luxus PP |
| Delene 5560 | Shanghai Lin Gen Rubber Materials Co., Ltd. | TPE | Delene |
| Sylvin 8707-80 Brown 7463 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |