FUDOWLITE® F5636F
| Category: | Phenolic , Phenolic |
| Manufacturer: | Fudow Co., Ltd. |
| Trademark: | FUDOWLITE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FlYFAK_FUDOWLITEF5636F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Examples of application
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.80 - 1.86 | g/cm³ | JIS K7112 |
| Apparent Density | 3.50 | g/cm³ | |
| Molding Shrinkage | 0.10 - 0.30 | % | JIS K6911 |
| Water Absorption (23°C, 24 hr) | 0.10 - 0.15 | % | JIS K6911 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 110 | JIS K6911 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 69.0 - 88.0 | MPa | JIS K6911 |
| Flexural Modulus | 12700 - 14700 | MPa | JIS K7171 |
| Flexural Stress | 118 - 137 | MPa | JIS K7171 |
| Compressive Stress | 196 - 216 | MPa | JIS K6911 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 6.4 - 7.4 | kJ/m² | JIS K7111 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | > 280 | °C | JIS K7191-1 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Insulation Resistance | JIS K6911 | ||
| after boiling | 1.0E+8 - 1.0E+9 | ohms | JIS K6911 |
| at ordinary state | 1.0E+8 - 1.0E+9 | ohms | JIS K6911 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Free Ammonia | % | JIS K7230 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 3.0 - 5.0 | kV/mm | JIS K6911 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.48 mm) | V-0 | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PTS PCA-2201NH | Polymer Technology and Services, LLC | PC+ABS | PTS |
| TRIREX® 3027IR | Samyang Corporation | PC | TRIREX® |
| ACCUTECH™ CP0436C10L1 | ACLO Compounders Inc. | PP Copolymer | ACCUTECH™ |
| Formolon® KVF | Formosa Plastics Corporation, U.S.A. | PVC Homopolymer | Formolon® |
| Dow Corning® C6-235 | Dow Corning Corporation | Silicone | Dow Corning® |