LNP™ COLORCOMP™ DX04401H compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ COLORCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FiXVa6_LNP-COLORCOMP-DX04401H-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP COLORCOMP DX04401H is an unfilled Polycarbonate. Added feature of this grade is: Healthcare. Also known as: LNP* COLORCOMP* Compound PDX-D-04401 Product reorder name: DX04401H |
| General Information | |
|---|---|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 12.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (24 hr) | 0.50 | % | ASTM D955 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.15 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.32 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2210 | MPa | ASTM D638 |
| Tensile Strength | |||
| Yield 2 | 62.0 | MPa | ASTM D638 |
| Yield | 62.0 | MPa | ISO 527-2 |
| Break 3 | 68.3 | MPa | ASTM D638 |
| Break | 68.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield 4 | 6.0 | % | ASTM D638 |
| Yield | 6.0 | % | ISO 527-2 |
| Break | 150 | % | ISO 527-2 |
| Flexural Modulus 5 | 2400 | MPa | ISO 178 |
| Flexural Stress | 98.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/2C | ||
| -30°C | 12 | kJ/m² | |
| 23°C | 25 | kJ/m² | |
| Notched Izod Impact | |||
| 23°C | 750 | J/m | ASTM D256 |
| 23°C 6 | 75 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact (23°C) | No Break | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 122 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 7 | 120 | °C | ISO 75-2/Af |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 2.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Constant (1 MHz) | 3.00 | ASTM D150 | |
| Dissipation Factor | ASTM D150 | ||
| 100 Hz | 1.0E-3 | ||
| 1 MHz | 2.0E-3 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Refractive Index | 1.586 | ASTM D542, ISO 489 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 310 to 321 | °C | |
| Front Temperature | 321 to 332 | °C | |
| Processing (Melt) Temp | 304 to 327 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 80*10*4 |
| 7 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ExxonMobil™ PP7064L1 | ExxonMobil Chemical | PP Impact Copolymer | ExxonMobil™ |
| Geon™ Vinyl Flexible 90250 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| LENTICULAR® 75LPI | Polycasa | PETG | LENTICULAR® |
| OmniLon™ PA6 U GR25 BK1000 | OMNI Plastics, LLC | Nylon 6 | OmniLon™ |
| Sylvin 9302-70FU White 1361 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |