DESLON™ 6 DSC150D
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | DESCO Co., Ltd. |
| Trademark: | DESLON™ 6 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Fh75pU_DESLON-6-DSC150D.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Descriptions: DESLON™ DSC150D is one of the brands which made by Polyamide6 that alloy with Polypropylene unfilled resin. It has good hinge property and low absorption property. Applications: DESLON™ DSC150D is applied to automotive clip and other parts which request low absorption feature and good hinge property. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.08 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 1.4 - 1.8 | % | |
| Water Absorption (23°C, 24 hr) | 1.0 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 59.6 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 63 | % | ASTM D638 |
| Flexural Modulus | 2500 | MPa | ASTM D790 |
| Flexural Strength | 83.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 69 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 149 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 68.0 | °C | ASTM D648 |
| Melting Temperature | 220 | °C | DSC |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 120 | °C | |
| Drying Time | 3.0 - 5.0 | hr | |
| Suggested Max Moisture | < 0.20 | % | |
| Rear Temperature | 240 - 250 | °C | |
| Middle Temperature | 250 - 260 | °C | |
| Front Temperature | 250 - 270 | °C | |
| Nozzle Temperature | 255 - 270 | °C | |
| Processing (Melt) Temp | 255 - 270 | °C | |
| Mold Temperature | 80.0 - 100 | °C |
| Injection instructions |
|---|
| Speed: 30 to 60%Pressure 1st: 30 to 70%Pressure 2nd: 30 to 70Holding Pressure: 10 to 30% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Reny® PG1050A | Mitsubishi Engineering-Plastics Corp | PARA | Reny® |
| Shandong Aobang TPU-Polyester 65-A | Shandong Aobang Chemical Technology Co.,Ltd. | TPU-Polyester | Shandong Aobang TPU-Polyester |
| Fainplast PVC RKS 430/W-OM | Fainplast Compounds S.r.l | PVC, Rigid | Fainplast PVC |
| Hy-Vin® VT662 | INEOS Compounds | PVC, Flexible | Hy-Vin® |
| CYCOLOY™ C1200HF resin | SABIC Innovative Plastics | PC+ABS | CYCOLOY™ |