ACCUTECH™ HP0334W10L1
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | ACLO Compounders Inc. |
| Trademark: | ACCUTECH™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Fg39Pf_ACCUTECH-HP0334W10L1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ACCUTECH™HP0334W10L1 is a polypropylene homopolymer (PP Homopoly) product containing 10% wollastonite (casio3). It is available in North America. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.968 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 6.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.1 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 89 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1600 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 35.0 | MPa | ASTM D638 |
| Fracture | 23.0 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 7.0 | % | ASTM D638 |
| Fracture | 28 | % | ASTM D638 |
| Flexural Modulus | 1600 | MPa | ASTM D790 |
| Flexural Strength | 36.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 54 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 107 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 60.0 | °C | ASTM D648 |
| Additional Information |
|---|
| Ash Content, ASTM D2584: 10% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Zytel® HTN 51G15HSL BK083 | DuPont Performance Polymers | PPA | Zytel® HTN |
| New-prene™ 9265N | Total Polymer Vision (Suzhou) Co., LTD | PP+EPDM | New-prene™ |
| Advanced Composites ATX832D | Advanced Composites, Inc. | TPO | Advanced Composites |
| BMC 695 | Bulk Molding Compounds, Inc. | Vinyl Ester | BMC |
| DiaAlloy TCL-1 | Mitsubishi Rayon America Inc. | PC | DiaAlloy |