Clearflex® FG 106
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Clearflex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ff0aB4_Clearflex-FG-106.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Clearflex FG 106 is a hexene copolymer linear low density polyethylene (C6-LLDPE), with antioxidants, suitable for blown film extrusion. Film manufactured with Clearflex FG 106 are characterised by excellent optical properties (haze and gloss), optimum sealing performances and high mechanical properties. Main Application Clearflex FG 106 is recommended for the production of agricultural film, blown stretch film coextruded or blended with LDPE. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.918 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (vs. Itself - Dynamic, Blown Film) | > 0.50 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Film Thickness - Recommended / Available | 10 to 50µm | ||
| Tensile Modulus | ISO 527-3 | ||
| 1% Secant, MD : 25 µm, Blown Film | 180 | MPa | |
| 1% Secant, TD : 25 µm, Blown Film | 210 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 25 µm, Blown Film | 9.00 | MPa | |
| TD : Yield, 25 µm, Blown Film | 10.0 | MPa | |
| MD : Break, 25 µm, Blown Film | 50.0 | MPa | |
| TD : Break, 25 µm, Blown Film | 45.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 25 µm, Blown Film | 600 | % | |
| TD : Break, 25 µm, Blown Film | 700 | % | |
| Dart Drop Impact 1(25 µm, Blown Film) | 160 | g | ISO 7765-1 |
| Elmendorf Tear Strength 2 | ISO 6383-2 | ||
| MD : 25.0 µm | 130.0 | kN/m | |
| TD : 25.0 µm | 230.0 | kN/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 101 | °C | ISO 306/A |
| Melting Temperature | 125 | °C | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.0 µm, Blown Film) | 60 | ASTM D2457 | |
| Haze (25.0 µm, Blown Film) | 10 | % | ISO 14782 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 to 230 | °C |
| Note Message | |
|---|---|
| 1 . | F50 |
| 2 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8215-90 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Andur 9-APF-LM/Curene3005/St105 | Anderson Development Company | PUR-Ester/TDI | Andur |
| Keltan® 6951C | LANXESS Buna GmbH | EPDM | Keltan® |
| Mitsui EPT™ 4045M | Mitsui Chemicals, Inc. | EPDM | Mitsui EPT™ |
| LNP™ THERMOCOMP™ PF00ASXS compound | SABIC Innovative Plastics | Nylon 6 | LNP™ THERMOCOMP™ |