Staramide P1000IX3
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Eurostar Engineering Plastics |
| Trademark: | Staramide |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FczSrx_Staramide-P1000IX3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Staramide P1000IX3 is an Impact Modified Polyamide 6 Injection Molding Resin (also known as P1000HI020 or Star X 2020) |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.10 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow (4.00 mm) | 1.4 | % | Internal Method |
| Water Absorption (23°C, 24 hr) | 2.3 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2000 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 50.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 4.1 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 1600 | MPa | ISO 178 |
| Flexural Stress | 61.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 2(23°C) | 36 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | No Break | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4 | |||
| 0.45 MPa, Unannealed, 64.0 mm Span | 136 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 64.0 mm Span | 48.0 | °C | ISO 75-2/Af |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 1.4E-4 | cm/cm/°C | |
| Transverse : 23 to 60°C | 1.6E-4 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 to 85.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 220 to 230 | °C | |
| Middle Temperature | 230 to 240 | °C | |
| Front Temperature | 240 to 250 | °C | |
| Processing (Melt) Temp | 240 to 250 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1385 TFE 13 SI 2 | RTP Company | PPS | RTP |
| RTP VLF 80207 EM HS | RTP Company | Nylon 66 | RTP |
| Sasol Polymers PP HNR101 | Sasol Polymers | PP Homopolymer | Sasol Polymers PP |
| Nypol® PA A3 G25 FR HS NTLA010 NR350 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Sylvin 9302-65 FU WHITE 1131 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |