Polimid A SG
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Poliblend S.p.a. |
| Trademark: | Polimid A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FcitD9_Polimid-A-SG.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polimid A SG is a Polyamide 66 (Nylon 66) material. It is available in Africa & Middle East, Asia Pacific, Europe, or Latin America. Primary attribute of Polimid A SG: Flame Rated. |
| General Information | |
|---|---|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.14 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 1.4 to 1.8 | % | |
| Water Absorption (23°C, 24 hr) | 1.2 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3200 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 85.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 5.0 | % | |
| Break | 60 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 5.0 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact Strength | No Break | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 210 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 90.0 | °C | ISO 75-2/A |
| Continuous Use Temperature 1 | 90.0 | °C | |
| Vicat Softening Temperature | 255 | °C | ISO 306/A120 |
| Ball Pressure Test (165°C) | Pass | IEC 60695-10-2 | |
| Melting Temperature | 260 | °C | DSC |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index | > 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | V-2 | ||
| 1.60 mm | V-2 | ||
| 3.20 mm | V-2 | ||
| Glow Wire Flammability Index (2.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (2.00 mm) | 725 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | > 3.0 | hr | |
| Processing (Melt) Temp | 260 to 280 | °C | |
| Mold Temperature | 70.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | Without Load |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P2845 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| RTP 200 AR 17 HS | RTP Company | Nylon 66 | RTP |
| Next Nylon 66 Prime Series PG50-01BK | Next Polymers Ltd. | Nylon 66 | Next Nylon 66 Prime Series |
| Arak HDPE EX3 (GM5010T2N) | Shazand (Arak) Petrochemical Corporation | HDPE | Arak HDPE |
| Karina GREEN COLOR CONCENTRATE 40/ 86-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |