4DUR® 9K22150
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | 4Plas |
| Trademark: | 4DUR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FcAGLG_4DUR-9K22150.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 4DUR 9K22150 is a Standard Flow 50% Glass Fibre Reinforced PBT |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.72 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Vertical flow direction | 0.80 | % | |
| Flow direction | 0.20 | % | |
| Water Absorption 1(Equilibrium, 23°C, 50% RH) | 0.10 | % | ISO 62 |
| Moisture Content | < 800 | ppm | ISO 960 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 18000 | MPa | ISO 527-2/5 |
| Tensile Stress (Break, 23°C) | 150 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 1.5 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180/1A | ||
| -30°C | 9.0 | kJ/m² | ISO 180/1A |
| 23°C | 11 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 220 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 210 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 215 | °C | ISO 306/B |
| Melting Temperature 2 | 225 | °C | ISO 11357 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | UL 94 | |
| 3.20 mm | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Processing (Melt) Temp | 250 - 270 | °C | |
| Mold Temperature | 60.0 - 100 | °C | |
| Injection Rate | Fast | ||
| Holding Pressure | 40.0 - 80.0 | MPa | |
| Screw Speed | < 200 | rpm |
| Injection instructions |
|---|
| Feed Throat Temperature: 50 - 70 °CBack Pressure: Low |
| Note Message | |
|---|---|
| 1 . | 24 Hrs |
| 2 . | 10 K/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMALENE WPP261 | Southern Polymer, Inc. | PP Impact Copolymer | PRIMALENE |
| Primefin V525 | Lucent Polymers, Inc. | PP, Unspecified | Primefin |
| Fainplast PVC CKL 0222 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Petrothene® LR763011 | LyondellBasell Industries | HDPE | Petrothene® |
| MACOMASS PP MM-PP HF 24 (40% Glass) | MACOMASS Verkaufs AG | PP Homopolymer | MACOMASS PP |